Ion beam-induced amorphous-to-tetragonal phase transformation and grain growth of nanocrystalline zirconia
Nanocrystalline zirconia has recently attracted extensive research interest due to its unique mechanical, thermal and electrical properties as compared to bulk zirconia counterparts, and it is of particular importance to control the phase stability of different polymorphs (amorphous, cubic, tetragonal and monoclinic phases) at different size regimes. In this paper, we performed ion beam bombardments on bilayers (amorphous and cubic) of pure nano-zirconia using 1 MeV Kr2+ irradiation. Transmission electron microscopy (TEM) analysis reveals that amorphous zirconia transforms to a tetragonal structure under irradiation at room temperature, suggesting that the tetragonal phase is more energetically favorable under these conditions. The final grain size of the tetragonal zirconia can be controlled by irradiation conditions. The irradiation-induced nanograins of tetragonal ZrO2 are stable at ambient conditions and maintain their physical integrity over a long period of time after irradiation. These results demonstrated that ion-beam modification methods provide the means to control the phase stability and structure of zirconia polymorphs.
- Research Organization:
- Pacific Northwest National Lab. (PNNL), Richland, WA (United States)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC05-76RL01830
- OSTI ID:
- 958463
- Report Number(s):
- PNNL-SA-66141; KC0201020; TRN: US1000351
- Journal Information:
- Nanotechnology, 20(24):245303, 1-7, Vol. 20, Issue 24
- Country of Publication:
- United States
- Language:
- English
Similar Records
Temperature and Size Effects on Radiation-Induced Phase Transformation in Monoclinic Nano-Sized Zirconia
Grain growth and phase stability of nanocrystalline cubic zirconia under ion irradiation