Chemically bonded phosphate ceramics : II, warm-temperature process for alumina ceramics.
This is the second of three papers on a dissolution model that describes the formation of chemically bonded phosphate ceramics. In this paper, we discuss the kinetics of formation of aluminum phosphate ceramics between 100 and 150 C. Using basic thermodynamic formulations, we calculated the temperatures of maximum solubility of alumina and its hydrated phases and predicted the temperatures of formation of ceramics. Differential thermal and X-ray diffraction analyses on samples made in the laboratory confirm these temperatures. The resulting ceramics of alumina bonded with aluminum phosphate (berlinite) show a high compressive strength of 16 000 psi. We have concluded that rapid evaporation of excess water in the slurry generates porosity in the ceramics, and that better processing methods are needed. A consolidation model is presented that describes the microstructure of the ceramic. It predicts that a very small amount of alumina must be converted to form the bonding phase; hence, the product is mostly alumina with a thin coating of berlinite on the surface of alumina particles.
- Research Organization:
- Argonne National Lab. (ANL), Argonne, IL (United States)
- Sponsoring Organization:
- FE
- DOE Contract Number:
- DE-AC02-06CH11357
- OSTI ID:
- 949396
- Report Number(s):
- ANL/ET/JA-40563; JACTAW; TRN: US201012%%192
- Journal Information:
- J. Am. Ceram. Soc., Vol. 86, Issue 11 ; Nov. 2003; ISSN 0002-7820
- Country of Publication:
- United States
- Language:
- ENGLISH
Similar Records
Phosphate-bonded glass cements for geothermal wells. Final report
Chemically bonded phosphate ceramics : part III : reduction mechanism and its application to iron phosphate ceramics.