The effects of long-term storage on the solderability of immersion silver coatings.
- Orion International Technologies, Inc., Albuquerque, NM
The solderability of an immersion Ag finish was evaluated after the exposure of test specimens to a Battelle Class II environment, which accelerates the storage conditions of light industrial surroundings. The solderability metric was the contact angle, (?C), as determined by the meniscometer/wetting balance technique. Auger surface and depth profile analyses were utilized to identify changes in the coating chemistry. The solderability test results indicate that there was no appreciable loss in solderability when the immersion Ag coated coupons were packaged in vapor phase corrosion (VPC) inhibitor bags and/or inhibitor bags with VPC inhibitor paper and aged for 8 hours, 1 week or 2 weeks in the Battelle Class II environment. An increase in surface carbon concentration after aging did not appear to significantly affect solderability.
- Research Organization:
- Sandia National Laboratories (SNL), Albuquerque, NM, and Livermore, CA (United States)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC04-94AL85000
- OSTI ID:
- 947305
- Report Number(s):
- SAND2006-0036C; TRN: US200909%%42
- Resource Relation:
- Conference: Proposed for presentation at the International Soldering and Brazing conference held April 23-26, 2006 in San Antonio, TX.
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effects of simulated storage on the solder wettability of inhibited substrates
Effects of simulated storage on the solder wettability of inhibited substrates