Texture, residual strain, and plastic deformation around scratches in alloy 600 using synchrotron x-ray Laue micro-diffraction.
Journal Article
·
· J. Nucl. Mater.
Deformation around two scratches in Alloy 600 (A600) was studied nondestructively using synchrotron Laue differential aperture X-ray microscopy. The orientation of grains and elastic strain distribution around the scratches were measured. A complex residual deviatoric elastic strain state was found to exist around the scratches. Heavy plastic deformation was observed up to a distance of 20 {micro}m from the scratches. In the region 20-30 {micro}m from the scratches the diffraction spots were heavily streaked and split indicating misoriented dislocation cell structures.
- Research Organization:
- Argonne National Lab. (ANL), Argonne, IL (United States)
- Sponsoring Organization:
- USDOE Office of Science (SC); Babcock & Wilson - Canada; Center for Materials and Manufacturing - Ontario; Dept. of Innovation, Industry and Regional Development - Australia
- DOE Contract Number:
- DE-AC02-06CH11357
- OSTI ID:
- 941492
- Report Number(s):
- ANL/XSD/JA-62899; JNUMAM; TRN: US0807437
- Journal Information:
- J. Nucl. Mater., Vol. 374, Issue 3 ; 2008; ISSN 0022-3115
- Country of Publication:
- United States
- Language:
- ENGLISH
Similar Records
X-ray Laue micro diffraction and neutron diffraction analysis of residual elastic strains and plastic deformation in a 1% uniaxial tensile tested nickel alloy 600 sample
Deformation behaviour of [001] oriented MgO using combined in-situ nano-indentation and micro-Laue diffraction
Residual strain orientation in rolled titanium determined with synchrotron X-ray Laue microdiffraction
Conference
·
Thu Jan 01 00:00:00 EST 2009
·
OSTI ID:941492
+5 more
Deformation behaviour of [001] oriented MgO using combined in-situ nano-indentation and micro-Laue diffraction
Journal Article
·
Tue Dec 19 00:00:00 EST 2017
· Acta Materialia
·
OSTI ID:941492
+6 more
Residual strain orientation in rolled titanium determined with synchrotron X-ray Laue microdiffraction
Journal Article
·
Wed Feb 01 00:00:00 EST 2023
· Journal of Applied Crystallography (Online)
·
OSTI ID:941492