Caustic Recycle from Hanford Tank Waste Using NaSICON Ceramic Membranes
A sodium (Na) Super Ion Conductor (NaSICON), has been studied at Pacific Northwest National Laboratory (PNNL) to investigate their ability to separate sodium from radioactively contaminated sodium salt solutions for treating U.S. Department of Energy (DOE) tank wastes. Ceramatec Inc. developed and fabricated a membrane disk containing a proprietary NAS-GY material formulation that was electrochemically tested in a bench-scale apparatus with both a simulant and a radioactive tank-waste solution to determine the membrane performance when removing sodium from DOE tank wastes. Implementing this sodium separation process can result in significant cost savings by reducing the disposal volume of low-activity wastes and by producing a 19M NaOH feedstock product for recycle into waste treatment processes such as sludge leaching, regenerating ion exchange resins, inhibiting corrosion in carbon-steel tanks, or retrieving tank wastes. In actual waste tests, average sodium transport rates of 10.3 kg/day/m2 were achieved at average sodium transport efficiencies of 99%. The membrane was found to be highly selective to sodium ions resulting in no detectable cation transport except Na and a small quantity (0.04% to 0.06%) of 137Cs. An average decontamination factor of 2000 was observed with respect to 137Cs. As expected, Gibbsite precipitation was observed as OH- ions were depleted from the tank waste.
- Research Organization:
- Pacific Northwest National Lab. (PNNL), Richland, WA (United States)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC05-76RL01830
- OSTI ID:
- 936595
- Report Number(s):
- PNNL-SA-58251; SSTEDS; 830403000; TRN: US0805596
- Journal Information:
- Separation Science and Technology, 43(9-10):2321-2342, Vol. 43, Issue 9-10; ISSN 0149-6395
- Country of Publication:
- United States
- Language:
- English
Similar Records
Sodium Recycle Economics for Waste Treatment Plant Operations
Salt splitting using ceramic membranes