EXPERIMENTAL EVALUATION OF DEFORMATION AND CONSTRAINT CHARACTERISTICS IN PRECRACKED CHARPY AND OTHER THREE-POINT BEND SPECIMENS
- ORNL
To enable determination of the fracture toughness reference temperature, T0, with reactor pressure vessel surveillance specimens, the precracked Charpy (PCVN) three-point bend, SE(B), specimen is of interest. Compared with the 25-mm (1 in.) thick compact, 1TC(T), specimen, tests with the PCVN specimen (10x10x55 mm) have resulted in T0 temperatures as much as 40 XC lower (a so-called specimen bias effect). The Heavy-Section Steel Irradiation (HSSI) Program at Oak Ridge National Laboratory developed a two-part project to evaluate the C(T) versus PCVN differences, (1) calibration experiments concentrating on test practices, and (2) a matrix of transition range tests with various specimen geometries and sizes, including 1T SE(B) and 1TC(T). The test material selected was a plate of A533 grade B class 1 steel. The calibration experiments included assessment of the computational validity of J-integral determinations, while the constraint characteristics of various specimen types and sizes were evaluated using key curves and notch strength determinations. The results indicate that J-integral solutions for the small PCVN specimen are comparable in terms of J-integral validity with 1T bend specimens. Regarding constraint evaluations, Phase I deformation is defined where plastic deformation is confined to crack tip plastic zone development, whereas Phase II deformation is defined where plastic hinging deformation develops. In Phase II deformation, the 0.5T SE(B) B B specimen (slightly larger than the PCVN specimen) consistently showed the highest constraint of all SE(B) specimens evaluated for constraint comparisons. The PCVN specimen begins the Phase II type of deformation at relatively low KR levels, with the result that KJc values above about 70 MPa m from precracked Charpy specimens are under extensive plastic hinging deformation.
- Research Organization:
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
- Sponsoring Organization:
- USDOE Office of Nuclear Energy (NE)
- DOE Contract Number:
- AC05-00OR22725
- OSTI ID:
- 931790
- Resource Relation:
- Conference: 2007 ASME Pressure Vessels and Piping Division Conference, San Antonio, TX, USA, 20070722, 20070726
- Country of Publication:
- United States
- Language:
- English
Similar Records
Single specimen method for determining upper shelf fracture toughness shifts using precracked Charpy specimens
Comparison between instrumented precracked Charpy and compact specimen tests of carbon steels