Dissolution kinetics of a sintered molybdenum coating applied on ceramics
Journal Article
·
· Protection of Metals
OSTI ID:91214
- Mendeleev Univ. of Chemical Engineering, Moscow (Russian Federation)
Using weighing and corrosion diagrams, the etching parameters are determined for a sintered M-21 molybdenum coating applied to VK 94-1 vacuum-tight ceramics. Dissolution of M-21 in an alkaline solution of potassium hexacyanoferrate(III) can be treated as a corrosion process proceeding with kinetic control.
- OSTI ID:
- 91214
- Journal Information:
- Protection of Metals, Vol. 30, Issue 6; Other Information: PBD: Nov-Dec 1994; TN: Translated from Zashchita Metallov; 30: No. 6, 657-658(1994)
- Country of Publication:
- United States
- Language:
- English
Similar Records
Optimization of the dissolution of molybdenum disks. FY-16 results
Dissolution kinetics of anorthite (CaAl/sub 2/Si/sub 2/O/sub 8/) and synthetic strontium feldspar (SrAl/sub 2/Si/sub 2/O/sub 8/) in aqueous solutions at temperatures below 100/sup 0/C: with applications to the geological disposal of radioactive nuclear wastes
Dissolution Kinetics of Titanium Pyrochlore Ceramics at 90?C by Single-Pass Flow-Through Experiments
Technical Report
·
Thu Sep 01 00:00:00 EDT 2016
·
OSTI ID:91214
+3 more
Dissolution kinetics of anorthite (CaAl/sub 2/Si/sub 2/O/sub 8/) and synthetic strontium feldspar (SrAl/sub 2/Si/sub 2/O/sub 8/) in aqueous solutions at temperatures below 100/sup 0/C: with applications to the geological disposal of radioactive nuclear wastes
Thesis/Dissertation
·
Fri Jan 01 00:00:00 EST 1982
·
OSTI ID:91214
Dissolution Kinetics of Titanium Pyrochlore Ceramics at 90?C by Single-Pass Flow-Through Experiments
Conference
·
Fri Dec 01 00:00:00 EST 2000
·
OSTI ID:91214
+1 more