Proceedings: Workshop on Initiation of Stress Corrosion Cracking Under LWR Conditions
Conference
·
OSTI ID:838373
Participants at this 1986 workshop discussed methods, such as electrochemical monitoring, for determining stress corrosion crack (SCC) initiation and for identifying variables involved in initiation. A survey of field occurrences of SCC revealed a correlation between fabrication-related defects and crack initiation.
- Research Organization:
- Electric Power Research Inst., Palo Alto, CA (US)
- Sponsoring Organization:
- Electric Power Research Institute (EPRI) (US)
- OSTI ID:
- 838373
- Report Number(s):
- EPRI-NP-5828; TRN: US200508%%80
- Resource Relation:
- Conference: Workshop on Initiation of Stress Corrosion Cracking Under LWR Conditions, Palo Alto, CA (US), 11/13/1986; Other Information: PBD: 1 May 1988
- Country of Publication:
- United States
- Language:
- English
Similar Records
Workshop on initiation of stress corrosion cracking under LWR conditions: Proceedings
Report on materials characterization center workshop on stress corrosion cracking for the Salt Repository Project, December 16-17, 1986, Seattle, Washington: Workshop summary
Role of Material Condition in Precursor Corrosion Damage and Stress Corrosion Crack Initiation Behavior of Alloy 600 in PWR Primary Water
Conference
·
Sun May 01 00:00:00 EDT 1988
·
OSTI ID:838373
Report on materials characterization center workshop on stress corrosion cracking for the Salt Repository Project, December 16-17, 1986, Seattle, Washington: Workshop summary
Conference
·
Mon Sep 01 00:00:00 EDT 1986
·
OSTI ID:838373
Role of Material Condition in Precursor Corrosion Damage and Stress Corrosion Crack Initiation Behavior of Alloy 600 in PWR Primary Water
Conference
·
Tue Jul 14 00:00:00 EDT 2020
·
OSTI ID:838373