Strength of tape cast and laminated ceramics
Journal Article
·
· Journal of the American Ceramic Society
- McMaster Univ., Hamilton, Ontario (Canada). Dept. of Materials Science and Engineering
Monolithic Al{sub 2}O{sub 3} ceramic laminates were fabricated via a tape casting process. The strength of the single tapes was compared with that of laminates, using biaxial flexure tests. The fracture stress was similar. However, the laminates presented a lower Weibull modulus. The feasibility of eliminating or diminishing void-type flaws present in the green tapes was also assessed. To this end, tapes were first punctured, then laminated and sintered, and the effect of these known flaws in the final ceramic was assessed in four-point flexure tests. The thermocompression of green tapes during laminate fabrication was found to modify the flaws to a more forgiving morphology.
- Sponsoring Organization:
- USDOE
- OSTI ID:
- 82627
- Journal Information:
- Journal of the American Ceramic Society, Vol. 78, Issue 6; Other Information: PBD: Jun 1995
- Country of Publication:
- United States
- Language:
- English
Similar Records
Strength and flaw elimination assessment in tape cast ceramic laminates
Tape cast Al2O3/ZrO2 composite laminates
Processing of tape-cast laminates prepared from fine alumina/zirconia powders
Conference
·
Thu Oct 01 00:00:00 EDT 1992
· Ceramic Engineering and Science Proceedings; (United States)
·
OSTI ID:82627
Tape cast Al2O3/ZrO2 composite laminates
Conference
·
Thu Oct 01 00:00:00 EDT 1992
· Ceramic Engineering and Science Proceedings; (United States)
·
OSTI ID:82627
+1 more
Processing of tape-cast laminates prepared from fine alumina/zirconia powders
Journal Article
·
Mon Aug 01 00:00:00 EDT 1994
· Journal of the American Ceramic Society; (United States)
·
OSTI ID:82627
+1 more