CO/sub 2/ corrosion of C-steel and 13Cr-steel in a particle laden fluid
Corrosion tests were carried out on C-steel (API 5L X70) and 13Cr steel (AISI 420) materials in a 3% NaCl solution containing sand particles (5000-9000 ppm) and saturated with CO/sub 2/ at defined partial pressure (0-0.3 MPa) and temperature (30-60/sup 0/C). The effect of residual O/sub 2/ content (10-1500 ppb) was further examined. Two flow geometries were studied: 1) undisturbed pipe flow and 2) submerged jet impinging (30-90/sup 0/) onto a flat plate. The effect of specimen surface treatment (shot-blasting or pickling) was examined with dry polished material as a reference. Weight-loss and electrochemical measurements were applied to determine average and instantaneous corrosion rates respectively. The results are discussed in relation to fluid flow conditions and the surface preparation/microstructure of materials tested.
- OSTI ID:
- 7203714
- Report Number(s):
- CONF-870314-
- Resource Relation:
- Conference: Corrosion '87, San Francisco, CA, USA, 9 Mar 1987
- Country of Publication:
- United States
- Language:
- English
Similar Records
Hydrogen permeation and diffusion in a 0. 2C-13Cr martensitic stainless steel
Stress Corrosion Cracking Response of 304 Stainless Steel in ASerated and Dearated Water
Related Subjects
42 ENGINEERING
CARBON DIOXIDE
CORROSIVE EFFECTS
CARBON STEELS
CORROSION RESISTANCE
CHROMIUM STEELS
PIPELINES
CORROSION
EROSION
SAND
DESTRUCTIVE TESTING
FLUID FLOW
HYDRODYNAMICS
MASS TRANSFER
SODIUM CHLORIDES
ALKALI METAL COMPOUNDS
ALLOYS
CARBON COMPOUNDS
CARBON OXIDES
CHALCOGENIDES
CHEMICAL REACTIONS
CHLORIDES
CHLORINE COMPOUNDS
CHROMIUM ALLOYS
FLUID MECHANICS
HALIDES
HALOGEN COMPOUNDS
IRON ALLOYS
IRON BASE ALLOYS
MATERIALS TESTING
MECHANICS
OXIDES
OXYGEN COMPOUNDS
SODIUM COMPOUNDS
STEELS
TESTING
360105* - Metals & Alloys- Corrosion & Erosion
420205 - Engineering- Transport & Storage Facilities- (1980-)