CO disintegration of stainless steel fiber-reinforced refractory castables
The effects of stainless steel fiber additions on the resistance of refractory castables to CO and steam were investigated. A series of high and intermediate alumina calcium aluminate-bonded castables was prepared containing several commercial stainless steel fibers. Compressive strength and abrasion resistance of the castables following exposure to high pressure carbon monoxide and steam at 500/sup 0/C were comparable to those of samples without stainless steel fibers. The addition of stainless steel fibers to refractory castables did not change the CO resistance of the castables unless they were fired in air before CO exposure. Airfiring creates oxide layer so the fibers which ultimately causes castable disintegration.
- Research Organization:
- Dept. of Materials Engineering, Virginia Polytechnic Institute, Blacksburg, VA 24061
- OSTI ID:
- 7034451
- Journal Information:
- Am. Ceram. Soc. Bull.; (United States), Vol. 65:9
- Country of Publication:
- United States
- Language:
- English
Similar Records
Stability of refractory castables in steam--N/sub 2/ and steam--CO atmospheres at 199/sup 0/C
Testing of refractories in CO-containing coal-gasification atmospheres. Final report. [Alumina concretes]
Related Subjects
ALUMINIUM OXIDES
CORROSION RESISTANCE
CARBON MONOXIDE
CORROSIVE EFFECTS
REFRACTORIES
STAINLESS STEELS
STEAM
ABRASION
AIR
ALUMINATES
CALCIUM COMPOUNDS
COMPARATIVE EVALUATIONS
COMPRESSION STRENGTH
FIBERS
HIGH TEMPERATURE
REINFORCED MATERIALS
TEMPERATURE EFFECTS
ALKALINE EARTH METAL COMPOUNDS
ALLOYS
ALUMINIUM COMPOUNDS
CARBON COMPOUNDS
CARBON OXIDES
CHALCOGENIDES
CHROMIUM ALLOYS
CORROSION RESISTANT ALLOYS
FLUIDS
GASES
IRON ALLOYS
IRON BASE ALLOYS
MATERIALS
MECHANICAL PROPERTIES
OXIDES
OXYGEN COMPOUNDS
STEELS
360205* - Ceramics
Cermets
& Refractories- Corrosion & Erosion
360105 - Metals & Alloys- Corrosion & Erosion