Thin film technology of high-critical-temperature superconducting electronics. Annual report 1 Aug 82-30 Oct 83
The objective of the first year's work was to investigate A15 superconductor/barrier oxide interfaces, identify oxide depth profiles, and determine resulting tunneling characteristics using soft tunnel junction counterelectrodes. Bilayers consisting of Nb and vanadium-silicon (A15) base electrodes and thin Y, Al, and Si barriers have been deposited in-situ and oxidized in humid air for up to three days. XPS analysis was used to compare the barrier coverage, uniformity, oxidation, and ability to protect the base electrode from oxidation for three deposition techniques: dc magnetron sputtering, dc diode sputtering, and reactive diode sputtering followed by pyrolysis. Y and Al have been found to be fully oxidized due to long oxidation times. In the above conditions the overlayers did not protect the superconductors from oxidation/hydration, and the surface of oxidized vanadium-silicon was also degraded by atomic segregation. The tunneling I-V characteristics exhibited very high leakage currents also suggestive of incomplete superconductor coverage by the metallic overlayer. Mo-Re was investigated for its potential as a high-critical-temperature counterelectrode. A very low oxidation rate was found indicating potential compatibility with yttrium hydroxide-sealed barriers. Low temperature growth (60 C) of MoRe (86 at. % Mo) with only a 5% decline in critical temperature has been demonstrated. Work will continue in a closed system to eliminate the base superconductor degradation, reduce leakage and study high-critical-temperature counterelectrodes.
- Research Organization:
- Westinghouse Electric Corp., Pittsburgh, PA (USA). Research and Development Center
- OSTI ID:
- 6830658
- Report Number(s):
- AD-A-136722/6
- Country of Publication:
- United States
- Language:
- English
Similar Records
Crystalline oxide tunnel barriers formed by thermal oxidation of aluminum overlayers on superconductor surfaces
Superconducting electronic-film structures. Semiannual report, 1 January-30 June 1985
Related Subjects
GENERAL PHYSICS
42 ENGINEERING
ELECTRONIC CIRCUITS
THIN FILMS
SUPERCONDUCTING DEVICES
ELECTRODES
FABRICATION
JOSEPHSON JUNCTIONS
MOLYBDENUM
NIOBIUM
OXIDATION
SPECTROSCOPY
SPUTTERING
SUPERCONDUCTORS
VANADIUM
CHEMICAL REACTIONS
ELEMENTS
FILMS
JUNCTIONS
METALS
SUPERCONDUCTING JUNCTIONS
TRANSITION ELEMENTS
420201* - Engineering- Cryogenic Equipment & Devices
420800 - Engineering- Electronic Circuits & Devices- (-1989)