OSTI ID:6787736
- comp.
Type 1020 mild steel, IF-steel[reg sign](registered trademark of Armco Steel Corporation, Middletown, Ohio), and TI-Namel were exposed in molten lithium hydride (LiH) at 800C for cumulative times approaching 300 h. Mild steel decarburized at an extreme rate with the affected area exhibiting tremendous grain growth. In contrast, IF-steels[reg sign] and TI-Namel do not experience decarburization or grain growth during identical exposures to LiH. All three steels experience net weight gains during extended exposure, and the data suggest that lithium penetration into the steel is the primary source of weight gain.
- Research Organization:
- Oak Ridge Y-12 Plant, TN (United States)
- Sponsoring Organization:
- USDOE; USDOE, Washington, DC (United States)
- DOE Contract Number:
- AC05-84OS21400
- OSTI ID:
- 6787736
- Report Number(s):
- Y-2457-3; ON: DE93011836
- Country of Publication:
- United States
- Language:
- English
Similar Records
Y-12 Development Division technical progress report. Part 3, Metal processing period ending December 1, 1992
Technology development for thin strip metal casting, Phase 2: Final technical report. [Melt spinning or planar flow casting]
Evaluation of Monobeam test program
Technical Report
·
Tue Jan 26 00:00:00 EST 1993
·
OSTI ID:6787736
Technology development for thin strip metal casting, Phase 2: Final technical report. [Melt spinning or planar flow casting]
Technical Report
·
Mon Mar 07 00:00:00 EST 1988
·
OSTI ID:6787736
Evaluation of Monobeam test program
Technical Report
·
Wed Mar 14 00:00:00 EST 1979
·
OSTI ID:6787736
Related Subjects
36 MATERIALS SCIENCE
CARBON STEELS
COMPATIBILITY
LITHIUM HYDRIDES
LOW ALLOY STEELS
STEELS
DECARBURIZATION
GRAIN GROWTH
LIQUIDS
PROGRESS REPORT
TEMPERATURE RANGE 1000-4000 K
WEIGHT
ALKALI METAL COMPOUNDS
ALLOYS
CHEMICAL REACTIONS
DOCUMENT TYPES
FLUIDS
HYDRIDES
HYDROGEN COMPOUNDS
IRON ALLOYS
IRON BASE ALLOYS
LITHIUM COMPOUNDS
TEMPERATURE RANGE
360105* - Metals & Alloys- Corrosion & Erosion
CARBON STEELS
COMPATIBILITY
LITHIUM HYDRIDES
LOW ALLOY STEELS
STEELS
DECARBURIZATION
GRAIN GROWTH
LIQUIDS
PROGRESS REPORT
TEMPERATURE RANGE 1000-4000 K
WEIGHT
ALKALI METAL COMPOUNDS
ALLOYS
CHEMICAL REACTIONS
DOCUMENT TYPES
FLUIDS
HYDRIDES
HYDROGEN COMPOUNDS
IRON ALLOYS
IRON BASE ALLOYS
LITHIUM COMPOUNDS
TEMPERATURE RANGE
360105* - Metals & Alloys- Corrosion & Erosion