CrMn underlayers for CoCrPt thin film media
Journal Article
·
· IEEE Transactions on Magnetics
OSTI ID:649527
- Intevac Inc., Santa Clara, CA (United States)
- Carnegie Mellon Univ., Pittsburgh, PA (United States). Data Storage Systems Center
An improved CoCrPt thin film medium or longitudinal magnetic recording which has a coercivity significantly greater than prior CoCrPt thin film media was investigated. A CrMn alloy underlayer was used, instead of the conventional Cr underlayer. A coercivity value of 4,280 Oe was easily reached in a CoCrPt film on a 50 nm thick CrMn underlayer as compared to 2,810 Oe with a pure Cr underlayer. It was found that the coercivity increase due to the Mn addition was realized if the substrates were preheated before the sputtering. Grain boundary interdiffusion of Mn from the underlayer to the magnetic layer may be the cause for the coercivity increase.
- Sponsoring Organization:
- USDOE, Washington, DC (United States)
- DOE Contract Number:
- FG02-90ER45423
- OSTI ID:
- 649527
- Report Number(s):
- CONF-980102-; ISSN 0018-9464; TRN: IM9825%%140
- Journal Information:
- IEEE Transactions on Magnetics, Vol. 34, Issue 4Pt1; Conference: 7. joint MMM-intermag conference, San Francisco, CA (United States), 6-9 Jan 1998; Other Information: PBD: Jul 1998
- Country of Publication:
- United States
- Language:
- English
Similar Records
FeAl underlayers for CoCrPt thin film longitudinal media
CoCrPt-SiO{sub 2} granular-type longitudinal media on Ru underlayer for sputtered tape applications
Manganese containing layer for magnetic recording media
Journal Article
·
Tue Apr 01 00:00:00 EST 1997
· Journal of Applied Physics
·
OSTI ID:649527
CoCrPt-SiO{sub 2} granular-type longitudinal media on Ru underlayer for sputtered tape applications
Journal Article
·
Tue Apr 01 00:00:00 EDT 2008
· Journal of Applied Physics
·
OSTI ID:649527
Manganese containing layer for magnetic recording media
Patent
·
Tue Nov 30 00:00:00 EST 1999
·
OSTI ID:649527