Effect of Cu, Mo, Si on the content of retained austenite of austempered ductile iron
Journal Article
·
· Scripta Metallurgica et Materialia
- Zhejiang Univ., Hangzhou (China). Dept. of Materials Science and Engineering
In this paper, the effects of Cu, Mo, Si contents on the volume fraction of retained austenite of austempered ductile iron (ADI) are analyzed exactly by X-ray diffraction, and the fracture modes of test samples with different volume fraction of retained austenite are investigated by SEM. It is shown that the retained austenite content increases with the content of copper, decreases with the content of molybdenum, and reaches the maximum with a certain content of silicon. When the retained austenite content decreases, the fracture modes of test samples change from ductile fracture to cleavage fracture.
- OSTI ID:
- 64350
- Journal Information:
- Scripta Metallurgica et Materialia, Vol. 32, Issue 9; Other Information: PBD: 1 May 1995
- Country of Publication:
- United States
- Language:
- English
Similar Records
Influence of microstructure on fracture toughness of austempered ductile iron
Effect of bainite transformation and retained austenite on mechanical properties of austempered spheroidal graphite cast steel
Effect of austempering time on mechanical properties of a low manganese austempered ductile iron
Journal Article
·
Tue Jul 01 00:00:00 EDT 1997
· Metallurgical and Materials Transactions. A, Physical Metallurgy and Materials Science
·
OSTI ID:64350
Effect of bainite transformation and retained austenite on mechanical properties of austempered spheroidal graphite cast steel
Journal Article
·
Sat Jun 01 00:00:00 EDT 1996
· Metallurgical Transactions, A
·
OSTI ID:64350
Effect of austempering time on mechanical properties of a low manganese austempered ductile iron
Journal Article
·
Sat Apr 01 00:00:00 EST 2000
· Journal of Materials Engineering and Performance
·
OSTI ID:64350