Structural characterization of YBa{sub 2}Cu{sub 3}O{sub 7{minus}{delta}}/Y{sub 2}O{sub 3} composite films
- Naval Research Laboratory, Washington, DC20375 (United States)
- Lawrence Livermore National Laboratory, Livermore, California94550 (United States)
- Northrop Grumman Science and Technology Center, Pittsburgh, Pennsylvania15235 (United States)
Using 4-circle x-ray diffraction and transmission electron microscopy, we have studied the microstructure and in-plane orientation of the phases present in thin film composite mixtures of YBa{sub 2}Cu{sub 3}O{sub 7{minus}{delta}} and Y{sub 2}O{sub 3}. We see a high degree of in-plane orientation and have verified a previous prediction for the in-plane order of Y{sub 2}BaCuO{sub 5} on (110) MgO. Transmission electron microscopy shows the composite films to be a mixture of two phases, with YBCO grain sizes of {approx}1{mu}m. We have also compared our observations of the in-plane order to the predictions of a modified near coincidence site lattice model. {copyright} {ital 1998 Materials Research Society.}
- OSTI ID:
- 627898
- Journal Information:
- Journal of Materials Research, Vol. 13, Issue 4; Other Information: PBD: Apr 1998
- Country of Publication:
- United States
- Language:
- English
Similar Records
Structural and chemical disorder near the Y[sub 2]BaCuO[sub 5]/YBa[sub 2]Cu[sub 3]O[sub 7[minus][delta]] interface and its possible relation to the flux-pinning behavior in melt-textured
Study of optical emission of the laser generated plasma of a Ag/YBa{sub 2}Cu{sub 3}O{sub 7{minus}{delta}} target and its consequences to oxide film growth