Evaluation of lithium-vanadium oxide cells. Technical report
Technical Report
·
OSTI ID:6117103
Hermetically sealed lithium-vanadium oxide cells were evaluated after one year of storage. From cell capacity measurements, excellent charge retention was found. The energy to weight and volume ratios did not change substantially during storage. The rate capability observed is within practical limits. At 0 degrees C the rate is 31 percent of that at room temperature.
- Research Organization:
- Army Electronics Research and Development Command, Fort Monmouth, NJ (USA). Electronics Technology/Devices Lab.
- OSTI ID:
- 6117103
- Report Number(s):
- AD-A-123720/5
- Country of Publication:
- United States
- Language:
- English
Similar Records
Evaluation of a new type of vanadium oxide from peroxo-polyvanadate as a cathode material for rechargeable lithium batteries
Lithium/sulfuryl chloride electrochemical cell
Silver oxide/zinc rechargeable lithium cells: A comparison with high energy density lithium/lithium cobalt oxide. Final report, 24 September 1989-1 March 1992
Journal Article
·
Wed Nov 01 00:00:00 EST 1995
· Journal of the Electrochemical Society
·
OSTI ID:6117103
Lithium/sulfuryl chloride electrochemical cell
Conference
·
Thu Mar 01 00:00:00 EST 1984
· J. Electrochem. Soc.; (United States)
·
OSTI ID:6117103
Silver oxide/zinc rechargeable lithium cells: A comparison with high energy density lithium/lithium cobalt oxide. Final report, 24 September 1989-1 March 1992
Technical Report
·
Wed Nov 01 00:00:00 EST 1995
·
OSTI ID:6117103
+2 more