Y-Ba-Cu-O thin films prepared by flash evaporation
Journal Article
·
· Appl. Phys. Lett.; (United States)
Oriented-Y-Ba-Cu-O thin films with thicknesses between 0.6 and 0.7 ..mu..m have been deposited on magnesium oxide substrates by the flash evaporation method. The deposition was made by dropping powders of sintered Y/sub 1/ Ba/sub 2/ Cu/sub 3/ O/sub 7/minus//ital x// onto a resistively heated tungsten boat. The as-deposited films were then annealed at 930 /degree/C in oxygen for 60 min. Annealed films were superconductors above 77 K and x-ray diffraction showed a preferred /ital c/-axis orientation. Increasing the annealing temperature to 945 /degree/C improved the texture of the films and the transition temperature of the superconductivity.
- Research Organization:
- Department of Physics, Syracuse University, Syracuse, New York 13244-1130(JP)
- OSTI ID:
- 6094417
- Journal Information:
- Appl. Phys. Lett.; (United States), Vol. 54:26
- Country of Publication:
- United States
- Language:
- English
Similar Records
Synthesis of high transition temperature superconducting Y-Ba-Cu-O films by radio-frequency plasma flash evaporation
The synthesis of superconducting Tl--Ca--Ba--Cu--oxide films by the reaction of spray deposited Ca--Ba--Cu--oxide precursors with Tl sub 2 O vapor in a two-zone reactor
High-current superconducting Tl{sub 1}Ba{sub 2}Ca{sub 2}Cu{sub 3}O{sub {ital y}} thick films on polycrystalline Ag by spin coating
Journal Article
·
Sat Dec 01 00:00:00 EST 1990
· IEEE Transactions on Plasma Science (Institute of Electrical and Electronics Engineers); (USA)
·
OSTI ID:6094417
The synthesis of superconducting Tl--Ca--Ba--Cu--oxide films by the reaction of spray deposited Ca--Ba--Cu--oxide precursors with Tl sub 2 O vapor in a two-zone reactor
Journal Article
·
Mon Jul 01 00:00:00 EDT 1991
· Journal of Materials Research; (USA)
·
OSTI ID:6094417
+3 more
High-current superconducting Tl{sub 1}Ba{sub 2}Ca{sub 2}Cu{sub 3}O{sub {ital y}} thick films on polycrystalline Ag by spin coating
Journal Article
·
Mon Jul 10 00:00:00 EDT 1995
· Applied Physics Letters
·
OSTI ID:6094417
+7 more
Related Subjects
36 MATERIALS SCIENCE
75 CONDENSED MATTER PHYSICS
SUPERCONDUCTIVITY AND SUPERFLUIDITY
BARIUM OXIDES
CRYSTAL STRUCTURE
TRANSITION TEMPERATURE
COPPER OXIDES
SUPERCONDUCTING FILMS
FABRICATION
YTTRIUM OXIDES
ANNEALING
EXPERIMENTAL DATA
PEROVSKITES
SINTERING
SUPERCONDUCTIVITY
THICKNESS
THIN FILMS
TUNGSTEN
VERY HIGH TEMPERATURE
ALKALINE EARTH METAL COMPOUNDS
BARIUM COMPOUNDS
CHALCOGENIDES
COPPER COMPOUNDS
DATA
DIMENSIONS
ELECTRIC CONDUCTIVITY
ELECTRICAL PROPERTIES
ELEMENTS
FILMS
HEAT TREATMENTS
INFORMATION
METALS
NUMERICAL DATA
OXIDES
OXYGEN COMPOUNDS
PHYSICAL PROPERTIES
THERMODYNAMIC PROPERTIES
TRANSITION ELEMENT COMPOUNDS
TRANSITION ELEMENTS
YTTRIUM COMPOUNDS
360201* - Ceramics
Cermets
& Refractories- Preparation & Fabrication
360204 - Ceramics
Cermets
& Refractories- Physical Properties
656100 - Condensed Matter Physics- Superconductivity
75 CONDENSED MATTER PHYSICS
SUPERCONDUCTIVITY AND SUPERFLUIDITY
BARIUM OXIDES
CRYSTAL STRUCTURE
TRANSITION TEMPERATURE
COPPER OXIDES
SUPERCONDUCTING FILMS
FABRICATION
YTTRIUM OXIDES
ANNEALING
EXPERIMENTAL DATA
PEROVSKITES
SINTERING
SUPERCONDUCTIVITY
THICKNESS
THIN FILMS
TUNGSTEN
VERY HIGH TEMPERATURE
ALKALINE EARTH METAL COMPOUNDS
BARIUM COMPOUNDS
CHALCOGENIDES
COPPER COMPOUNDS
DATA
DIMENSIONS
ELECTRIC CONDUCTIVITY
ELECTRICAL PROPERTIES
ELEMENTS
FILMS
HEAT TREATMENTS
INFORMATION
METALS
NUMERICAL DATA
OXIDES
OXYGEN COMPOUNDS
PHYSICAL PROPERTIES
THERMODYNAMIC PROPERTIES
TRANSITION ELEMENT COMPOUNDS
TRANSITION ELEMENTS
YTTRIUM COMPOUNDS
360201* - Ceramics
Cermets
& Refractories- Preparation & Fabrication
360204 - Ceramics
Cermets
& Refractories- Physical Properties
656100 - Condensed Matter Physics- Superconductivity