Microscopic study of alkali-activated fly ash
- Technion, Haifa (Israel). National Building Research Inst.
The activation mechanism of fly ash in a basic environment was studied as a means to improve the reactivity of fly ash in blended cements. The experimental program included activation of fly ash by a strong base (NaOH) at different concentrations, temperatures, and water-to-fly ash ratios. It was found that the degree of reactivity, as shown by the compressive strength, increases with increasing concentration of the base (up to 4 mol of NaOH) and curing temperature (up to 90 C). Lowering the sodium hydroxide to fly ash ratio by lowering the water/fly ash ratio, while maintaining the solution concentration constant yielded a lower compressive strength in spite of the lower porosity, and the high concentration of the solution. These results indicate that activation of fly ash in blended cements depends not only on the pH of the activating ambiance but also on the ratio between the latter and the fly ash.
- OSTI ID:
- 605722
- Journal Information:
- Cement and Concrete Research, Vol. 28, Issue 2; Other Information: PBD: Feb 1998
- Country of Publication:
- United States
- Language:
- English
Similar Records
Utilization of blended fluidized bed combustion (FBC) ash and pulverized coal combustion (PCC) fly ash in geopolymer
Preparation and characterization of a hybrid alkaline binder based on a fly ash with no commercial value