Regarding the SiC particulates size associated microstructural characteristics on the aging behavior of Al-4.5Cu metallic matrix
- National Univ. of Singapore (Singapore). Dept. of Mechanical and Production Engineering
In this study, aging characteristics of an aluminum-based metallic matrix reinforced with two different sizes of silicon carbide were investigated. The results showed similar aging kinetics in the case of unreinforced samples and composite samples containing coarser (34.4 {micro}m) SiC particulates and accelerated aging kinetics in the case of composite samples containing finer (8 {micro}m) SiC particulates. Results of microstructural characterization studies show that composite samples containing finer SiC particulates exhibited finer grain size, lower porosity, reduced cluster-to-particulate-size ratio, and superior interfacial integrity. The accelerated aging kinetics exhibited by composite samples containing a distribution of finer SiC particulates, when compared to the unreinforced and reinforced samples containing a distribution of coarser SiC particulates, were rationalized in terms of their microstructural characteristics.
- OSTI ID:
- 605685
- Journal Information:
- Materials Research Bulletin, Vol. 33, Issue 2; Other Information: PBD: Feb 1998
- Country of Publication:
- United States
- Language:
- English
Similar Records
Age-hardening behavior of Al-Cu-SiC[sub p] composites synthesized by casting route
The relationships between microstructure and deformation of SiC particulate reinforced Al-6061