Superconducting-wire fabrication. Final report
Technical Report
·
OSTI ID:5899355
Experiments were done leading to the fabrication of high-temperature superconducting composite wire. Bulk superconductor was characterized by using optical microscopy, scanning electron microscopy, and energy-dispersive x-ray spectroscopy. The chemical compatibility of superconducting materials with a number of metal sheathing candidates was tested, with silver offering the best compatibility. Wire was fabricated by drawing 0.250-inch-diameter silver tubing packed with superconducting powder. Single core wires were drawn to 0.037-inch diameter. The best critical current performance (660 A/cm2) for leaded bismuth 2-2-2-3 material was achieved by flattening single-core wire before heat treatment.
- Research Organization:
- Naval Ocean Systems Center, San Diego, CA (USA)
- OSTI ID:
- 5899355
- Report Number(s):
- AD-A-228012/1/XAB; NOSC/TR-1347
- Resource Relation:
- Other Information: Original contains color plates: All DTIC and NTIS reproductions will be in black and white
- Country of Publication:
- United States
- Language:
- English
Similar Records
High T/sub C/ superconductors: composite wire fabrication
Recent progress in BPSCCO wire fabrication and applications prototypes
FABRICATION OF BERYLLIUM FINE WIRE. Final Report. Technical Report 200- 228
Journal Article
·
Mon Jul 20 00:00:00 EDT 1987
· Appl. Phys. Lett.; (United States)
·
OSTI ID:5899355
+2 more
Recent progress in BPSCCO wire fabrication and applications prototypes
Journal Article
·
Sun Jun 01 00:00:00 EDT 1997
· Advances in Cryogenic Engineering
·
OSTI ID:5899355
FABRICATION OF BERYLLIUM FINE WIRE. Final Report. Technical Report 200- 228
Technical Report
·
Sat Apr 01 00:00:00 EST 1961
·
OSTI ID:5899355
Related Subjects
75 CONDENSED MATTER PHYSICS
SUPERCONDUCTIVITY AND SUPERFLUIDITY
SUPERCONDUCTING WIRES
FABRICATION
COMPATIBILITY
COMPOSITE MATERIALS
COVERINGS
DISPERSIONS
ELECTRON MICROSCOPY
ENERGY
HEAT TREATMENTS
HIGH TEMPERATURE
METALS
PERFORMANCE
POWDERS
PROGRESS REPORT
SCANNING ELECTRON MICROSCOPY
SILVER
SUPERCONDUCTING COMPOSITES
X-RAY SPECTROSCOPY
DOCUMENT TYPES
ELEMENTS
MATERIALS
MICROSCOPY
SPECTROSCOPY
TRANSITION ELEMENTS
WIRES
426001* - Engineering- Superconducting Devices & Circuits- (1990-)
SUPERCONDUCTIVITY AND SUPERFLUIDITY
SUPERCONDUCTING WIRES
FABRICATION
COMPATIBILITY
COMPOSITE MATERIALS
COVERINGS
DISPERSIONS
ELECTRON MICROSCOPY
ENERGY
HEAT TREATMENTS
HIGH TEMPERATURE
METALS
PERFORMANCE
POWDERS
PROGRESS REPORT
SCANNING ELECTRON MICROSCOPY
SILVER
SUPERCONDUCTING COMPOSITES
X-RAY SPECTROSCOPY
DOCUMENT TYPES
ELEMENTS
MATERIALS
MICROSCOPY
SPECTROSCOPY
TRANSITION ELEMENTS
WIRES
426001* - Engineering- Superconducting Devices & Circuits- (1990-)