Low-pH stress corrosion crack propagation in API X-65 line pipe steel
Journal Article
·
· Corrosion (Houston); (United States)
- Cortest Columbus Technologies, Inc., Columbus, OH (United States)
Preliminary results of ongoing crack growth studies being performed on an API X-65 line pipe steel in a low-pH cracking environment were reported. Objectives were to reproduce low-pH crack propagation in the laboratory, to identify a crack driving force parameter, and to evaluate the influence of environmental and mechanical parameters on crack growth. A J-integral test technique was used in the study. Significant crack growth was observed. The parameter J appeared to be a good driving force parameter to describe crack growth.
- OSTI ID:
- 5842336
- Journal Information:
- Corrosion (Houston); (United States), Vol. 49:10; ISSN 0010-9312
- Country of Publication:
- United States
- Language:
- English
Similar Records
Low-pH stress corrosion cracking of natural gas pipelines
Mechanical and metallurgical effects on low-pH stress corrosion cracking of natural gas pipelines
Stress corrosion cracking of X-60 line pipe steel in a carbonate-bicarbonate solution
Book
·
Sat Dec 31 00:00:00 EST 1994
·
OSTI ID:5842336
Mechanical and metallurgical effects on low-pH stress corrosion cracking of natural gas pipelines
Book
·
Fri Dec 01 00:00:00 EST 1995
·
OSTI ID:5842336
Stress corrosion cracking of X-60 line pipe steel in a carbonate-bicarbonate solution
Journal Article
·
Wed Feb 01 00:00:00 EST 1995
· Corrosion (Houston); (United States)
·
OSTI ID:5842336
Related Subjects
36 MATERIALS SCIENCE
03 NATURAL GAS
PIPELINES
FRACTURE MECHANICS
STEELS
CRACK PROPAGATION
STRESS CORROSION
NATURAL GAS
PH VALUE
ALLOYS
CHEMICAL REACTIONS
CORROSION
ENERGY SOURCES
FLUIDS
FOSSIL FUELS
FUEL GAS
FUELS
GAS FUELS
GASES
IRON ALLOYS
IRON BASE ALLOYS
MECHANICS
360105* - Metals & Alloys- Corrosion & Erosion
360103 - Metals & Alloys- Mechanical Properties
032000 - Natural Gas- Transport
Handling
& Storage
03 NATURAL GAS
PIPELINES
FRACTURE MECHANICS
STEELS
CRACK PROPAGATION
STRESS CORROSION
NATURAL GAS
PH VALUE
ALLOYS
CHEMICAL REACTIONS
CORROSION
ENERGY SOURCES
FLUIDS
FOSSIL FUELS
FUEL GAS
FUELS
GAS FUELS
GASES
IRON ALLOYS
IRON BASE ALLOYS
MECHANICS
360105* - Metals & Alloys- Corrosion & Erosion
360103 - Metals & Alloys- Mechanical Properties
032000 - Natural Gas- Transport
Handling
& Storage