Fatigue crack retardation of high strength steel in saltwater
A high strength steel was studied in 3 percent saltwater to investigate the effects of a corrosive environment and sheer thickness on fatigue crack propagation behavior following the application of a single tensile overload. Experiments were carried out under sinusoidally varying loads at a load ratio of 0 and frequency of 10 H /SUB z/ . A single tensile overload was found to cause delayed retardation, and the crack propagation rate at first increased, followed by fairly rapid decrease to a minimum value and then increased gradually to its steady-state value, just as it did in air. The overload affected zone size and the retardation cycles increased with decreasing sheet thickness, just as they did in air. However, the zone size and the cycles were larger in 3 percent saltwater than in air. Since the crack propagation rates through the overload affected zone were not affected by the test environment, the longer retardation cycles in 3 percent saltwater were attributed to an enlargement of the overload affected zone size. The crack propagation behavior following the application of a single tensile overload in 3 percent saltwater was well explained by the crack closure concept.
- Research Organization:
- Department of Mechanical Engineering, Faculty of Engineering, Gifu University, 1-1 Yanagido, Gifu
- OSTI ID:
- 5783785
- Journal Information:
- J. Eng. Mater. Technol.; (United States), Vol. 105:2
- Country of Publication:
- United States
- Language:
- English
Similar Records
Fatigue crack retardation in PM aluminum alloys AA8022 and AA5091. Ph.D. Thesis
Effect of load excursions and specimen thickness on crack closure measurements