Processing and characterization of functionally graded TiB{sub 2}/NiAl produced by the combustion synthesis process
Conference
·
OSTI ID:567854
- Colorado School of Mines, Golden, CO (United States)
NiAl/TiB{sub 2} functionally graded composites were produced by the combustion synthesis process. X-ray diffraction and optical microscopy were used to characterize the microstructure. Hardness measurement at room temperature and 900{degrees}C were used to probe the mechanical properties. The Vickers hardness at room temperature varies linearly with TiB{sub 2} content. However, the high temperature hardness varies non-linearly with TiB{sub 2} content and is sensitive to microstructure. In particular, plastic flow in NiAl at high temperature depends on TiB{sub 2} particle size.
- OSTI ID:
- 567854
- Report Number(s):
- CONF-9604124-; TRN: 98:000175-0003
- Resource Relation:
- Conference: 98. annual meeting of the American Ceramic Society, Indianapolis, IN (United States), 14-17 Apr 1996; Other Information: PBD: 1997; Related Information: Is Part Of Ceramic transactions: Functionally graded materials - manufacture, properties, and applications. Volume 76; Ghosh, A.; Miyamoto, Yoshinari; Reimanis, I.; Lannutti, J.J. [eds.]; PB: 200 p.
- Country of Publication:
- United States
- Language:
- English
Similar Records
Compression behavior and interfaces of NiAl-TiB[sub 2] in situ composites
High temperature x-ray diffraction investigation of nickel-rich NiAl and NiAl-TiB[sub 2]
Comparative investigation on microstructures and mechanical properties of (TiB + TiC)/Ti-6Al-4V composites from Ti-B4C-C and Ti-TiB2-TiC systems
Journal Article
·
Tue Nov 01 00:00:00 EST 1994
· Scripta Metallurgica et Materialia; (United States)
·
OSTI ID:567854
+2 more
High temperature x-ray diffraction investigation of nickel-rich NiAl and NiAl-TiB[sub 2]
Journal Article
·
Fri Apr 01 00:00:00 EST 1994
· Acta Metallurgica et Materialia; (United States)
·
OSTI ID:567854
Comparative investigation on microstructures and mechanical properties of (TiB + TiC)/Ti-6Al-4V composites from Ti-B4C-C and Ti-TiB2-TiC systems
Journal Article
·
Fri Jun 15 00:00:00 EDT 2018
· Materials Characterization
·
OSTI ID:567854
+3 more