Kinetics and mechanisms of creep crack growth in a creep-resisting steel
Journal Article
·
· Strength Mater. (Engl. Transl.); (United States)
OSTI ID:5633708
This paper discusses the nature of kinetic diagrams of growth of fatigue cracks in the temperature range typical of operation of important components of power equipment and examines the proportion of the incubation period of crack growth in the total life. The relationship of the kinetic diagrams of crack growth with the fracture mechanisms are examined and the effect of running life on creep crack propagation is reviewed.
- Research Organization:
- Institute of Strength Problems, Academy of Sciences of the Ukranian SSR, Kiev
- OSTI ID:
- 5633708
- Journal Information:
- Strength Mater. (Engl. Transl.); (United States), Vol. 17:6
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effects of neutron irradiation on fatigue and creep-fatigue crack propagation in type 316 stainless steel at 649 degree C produced no significant effect on the crack propagation rate when compared with unirradiated steel tested at 649 degree C
Characterization of Creep-Fatigue Crack Growth in Alloy 709 and Prediction of Service Lives in Nuclear Reactor Components (Final Report)
The influence of plasticity-induced crack closure on creep-fatigue crack growth in two heat-resistant steels
Conference
·
Thu Jan 01 00:00:00 EST 1981
· Am. Soc. Test. Mater., Spec. Tech. Publ.; (United States)
·
OSTI ID:5633708
Characterization of Creep-Fatigue Crack Growth in Alloy 709 and Prediction of Service Lives in Nuclear Reactor Components (Final Report)
Technical Report
·
Tue Apr 30 00:00:00 EDT 2019
·
OSTI ID:5633708
+6 more
The influence of plasticity-induced crack closure on creep-fatigue crack growth in two heat-resistant steels
Journal Article
·
Fri Apr 05 00:00:00 EDT 2019
· International Journal of Fatigue
·
OSTI ID:5633708
+4 more
Related Subjects
36 MATERIALS SCIENCE
STEELS
CRACK PROPAGATION
CREEP
FRACTURE MECHANICS
DESTRUCTIVE TESTING
FRACTURE PROPERTIES
MECHANICAL TESTS
ROTORS
SERVICE LIFE
STRESS INTENSITY FACTORS
THERMAL CYCLING
THERMAL DEGRADATION
THERMAL FATIGUE
THERMAL POWER PLANTS
THERMAL STRESSES
ALLOYS
FATIGUE
IRON ALLOYS
IRON BASE ALLOYS
MATERIALS TESTING
MECHANICAL PROPERTIES
MECHANICS
POWER PLANTS
STRESSES
TESTING
360103* - Metals & Alloys- Mechanical Properties
STEELS
CRACK PROPAGATION
CREEP
FRACTURE MECHANICS
DESTRUCTIVE TESTING
FRACTURE PROPERTIES
MECHANICAL TESTS
ROTORS
SERVICE LIFE
STRESS INTENSITY FACTORS
THERMAL CYCLING
THERMAL DEGRADATION
THERMAL FATIGUE
THERMAL POWER PLANTS
THERMAL STRESSES
ALLOYS
FATIGUE
IRON ALLOYS
IRON BASE ALLOYS
MATERIALS TESTING
MECHANICAL PROPERTIES
MECHANICS
POWER PLANTS
STRESSES
TESTING
360103* - Metals & Alloys- Mechanical Properties