An analysis of the deformation approach to calculation of the life of hydrogen impregnated 1Kh16N4B steel in low-cycle fatigue
Journal Article
·
· Strength Mater. (Engl. Transl.); (United States)
OSTI ID:5633651
This paper presents the results of experimental investigations and an analysis of the applicability of the deformation approach for calculation of the life of 1Kh16N4B steel in low-cycle fatigue. Hydrogen impregnation was done with use of cathodic polarization in a special cell with a polarization current density of 35 mA/cm/sup 2/ for 60 min. The test results are presented, and it can be seen that the influence of hydrogen absorption significantly changes the life of 1Kh16N4B steel, but the Coffin-Kavomoto criterion does not give satisfactory results.
- Research Organization:
- Krasrodar Polytechnic Institute
- OSTI ID:
- 5633651
- Journal Information:
- Strength Mater. (Engl. Transl.); (United States), Vol. 17:5
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effect of aqueous operating media on the low-cycle fatigue of constructional steels
Application of frequency-modified life approach to the low-cycle fatigue behavior of Type 304 stainless steel. [1100 °F]
Effectiveness of inhibitors in the hydrogen impregnation of low-carbon steel being elastically deformed
Journal Article
·
Sat Jan 01 00:00:00 EST 1983
· Chem. Pet. Eng. (Engl. Transl.); (United States)
·
OSTI ID:5633651
Application of frequency-modified life approach to the low-cycle fatigue behavior of Type 304 stainless steel. [1100 °F]
Technical Report
·
Sat May 01 00:00:00 EDT 1976
·
OSTI ID:5633651
Effectiveness of inhibitors in the hydrogen impregnation of low-carbon steel being elastically deformed
Journal Article
·
Fri Nov 01 00:00:00 EST 1985
· Sov. Mater. Sci. (Engl. Transl.); (United States)
·
OSTI ID:5633651
Related Subjects
36 MATERIALS SCIENCE
PRESSURE VESSELS
DEFORMATION
FATIGUE
HYDROGEN EMBRITTLEMENT
STEEL-1KH16N4B
DESTRUCTIVE TESTING
HYDROGEN
IMPREGNATION
POLARIZATION
SERVICE LIFE
STRESS ANALYSIS
STRESS INTENSITY FACTORS
ALLOYS
CHROMIUM ALLOYS
CHROMIUM STEELS
CHROMIUM-NICKEL STEELS
CONTAINERS
CORROSION RESISTANT ALLOYS
ELEMENTS
EMBRITTLEMENT
IRON ALLOYS
IRON BASE ALLOYS
MANGANESE ADDITIONS
MANGANESE ALLOYS
MATERIALS TESTING
MECHANICAL PROPERTIES
NICKEL ALLOYS
NIOBIUM ADDITIONS
NIOBIUM ALLOYS
NONMETALS
SILICON ADDITIONS
SILICON ALLOYS
STAINLESS STEELS
STEELS
TESTING
360103* - Metals & Alloys- Mechanical Properties
PRESSURE VESSELS
DEFORMATION
FATIGUE
HYDROGEN EMBRITTLEMENT
STEEL-1KH16N4B
DESTRUCTIVE TESTING
HYDROGEN
IMPREGNATION
POLARIZATION
SERVICE LIFE
STRESS ANALYSIS
STRESS INTENSITY FACTORS
ALLOYS
CHROMIUM ALLOYS
CHROMIUM STEELS
CHROMIUM-NICKEL STEELS
CONTAINERS
CORROSION RESISTANT ALLOYS
ELEMENTS
EMBRITTLEMENT
IRON ALLOYS
IRON BASE ALLOYS
MANGANESE ADDITIONS
MANGANESE ALLOYS
MATERIALS TESTING
MECHANICAL PROPERTIES
NICKEL ALLOYS
NIOBIUM ADDITIONS
NIOBIUM ALLOYS
NONMETALS
SILICON ADDITIONS
SILICON ALLOYS
STAINLESS STEELS
STEELS
TESTING
360103* - Metals & Alloys- Mechanical Properties