Corrosion cracking
Various papers on corrosion cracking are presented. The topics addressed include: unique case studies on hydrogen embrittlement failures in components used in aeronautical industry; analysis of subcritical cracking in a Ti-5Al-2.5Sn liquid hydrogen control valve; corrosion fatigue and stress corrosion cracking of 7475-T7351 aluminum alloy; effects of salt water environment and loading frequency on crack initiation in 7075-T7651 aluminum alloy and Ti-6Al-4V; stress corrosion cracking of 4340 steel in aircraft ignition starter residues. Also discussed are: stress corrosion cracking of a titanium alloy in a hydrogen-free environment; automation in corrosion fatigue crack growth rate measurements; the breaking load method, a new approach for assessing resistance to growth of early stage stress corrosion cracks; stress corrosion cracking properties of 2090 Al-Li alloy; repair welding of cracked free machining Invar 36; radial bore cracks in rotating disks.
- OSTI ID:
- 5485758
- Country of Publication:
- United States
- Language:
- English
Similar Records
Evaluation of surface fatigue cracks using Rayleigh waves. Ph.D. Thesis
Tensile properties of cast titanium alloys: Titanium-6Al-4V ELI and Titanium-5Al-2. 5Sn ELI
Related Subjects
ALLOYS
CRACKS
ALUMINIUM ALLOYS
CORROSION
CRACK PROPAGATION
FAILURES
FATIGUE
HYDROGEN EMBRITTLEMENT
LASER WELDING
LEADING ABSTRACT
MEETINGS
STRESS CORROSION
TIN ALLOYS
TITANIUM ALLOYS
VANADIUM ALLOYS
ABSTRACTS
CHEMICAL REACTIONS
DOCUMENT TYPES
EMBRITTLEMENT
FABRICATION
JOINING
MECHANICAL PROPERTIES
WELDING
360103* - Metals & Alloys- Mechanical Properties