Selective Fischer-Tropsch synthesis on metal powder catalysts prepared by the potassium reduction of halides in THF
Journal Article
·
· J. Catal.; (United States)
Metal powders such as Fe, Co, Ni, Fe-Co, and Fe-Ni prepared by reducing metal iodides or bromides with potassium metal in refluxing THF were used as catalysts for Fischer-Tropsch syntheses. These metal powders contained very small particles and have BET surface areas (28-36 m/sup 2//g). The metal powder catalysts, such as Fe and Fe-Co (80:20), gave 1-butene with more than 35 wt% selectivity at a rather high CO conversion of over 10 wt% at 533-553 K, while products on the Co catalyst obeyed conventional Schulz-Flory type distribution. The Ni catalyst showed little activity. Effects of reaction variables (temperature, H/sub 2//CO feed gas ratio, and composition of Fe-Co) were investigated.
- Research Organization:
- Osaka Univ., Japan
- OSTI ID:
- 5397512
- Journal Information:
- J. Catal.; (United States), Vol. 105:2
- Country of Publication:
- United States
- Language:
- English
Similar Records
Iron oxide pillared clay with large gallery height: Synthesis and properties as a Fischer-Tropsch catalyst
Catalyst and reactor development for a liquid-phase Fischer-Tropsch process. Quarterly technical progress report, 1 January 1982-31 March 1982
Fischer-Tropsch synthesis over reduced and unreduced iron oxide catalysts
Journal Article
·
Mon Jul 01 00:00:00 EDT 1991
· Journal of Catalysis; (United States)
·
OSTI ID:5397512
Catalyst and reactor development for a liquid-phase Fischer-Tropsch process. Quarterly technical progress report, 1 January 1982-31 March 1982
Technical Report
·
Thu Apr 01 00:00:00 EST 1982
·
OSTI ID:5397512
+1 more
Fischer-Tropsch synthesis over reduced and unreduced iron oxide catalysts
Journal Article
·
Wed Jan 01 00:00:00 EST 1986
· J. Catal.; (United States)
·
OSTI ID:5397512
Related Subjects
01 COAL, LIGNITE, AND PEAT
COBALT
CATALYTIC EFFECTS
COBALT ALLOYS
FISCHER-TROPSCH SYNTHESIS
CATALYSIS
IRON
IRON ALLOYS
NICKEL
NICKEL ALLOYS
BIMETALS
BUTENES
CARBON MONOXIDE
CHEMICAL COMPOSITION
CHEMICAL PREPARATION
CHEMICAL REACTION YIELD
COMPARATIVE EVALUATIONS
HYDROGEN
LOADING RATE
PERFORMANCE TESTING
SYNTHESIS
TEMPERATURE DEPENDENCE
TETRAHYDROFURAN
ALKENES
ALLOYS
CARBON COMPOUNDS
CARBON OXIDES
CHALCOGENIDES
CHEMICAL REACTIONS
ELEMENTS
FURANS
HETEROCYCLIC COMPOUNDS
HYDROCARBONS
METALS
NONMETALS
ORGANIC COMPOUNDS
ORGANIC OXYGEN COMPOUNDS
OXIDES
OXYGEN COMPOUNDS
TESTING
TRANSITION ELEMENTS
YIELDS
010408* - Coal
Lignite
& Peat- C1 Processes- (1987-)
COBALT
CATALYTIC EFFECTS
COBALT ALLOYS
FISCHER-TROPSCH SYNTHESIS
CATALYSIS
IRON
IRON ALLOYS
NICKEL
NICKEL ALLOYS
BIMETALS
BUTENES
CARBON MONOXIDE
CHEMICAL COMPOSITION
CHEMICAL PREPARATION
CHEMICAL REACTION YIELD
COMPARATIVE EVALUATIONS
HYDROGEN
LOADING RATE
PERFORMANCE TESTING
SYNTHESIS
TEMPERATURE DEPENDENCE
TETRAHYDROFURAN
ALKENES
ALLOYS
CARBON COMPOUNDS
CARBON OXIDES
CHALCOGENIDES
CHEMICAL REACTIONS
ELEMENTS
FURANS
HETEROCYCLIC COMPOUNDS
HYDROCARBONS
METALS
NONMETALS
ORGANIC COMPOUNDS
ORGANIC OXYGEN COMPOUNDS
OXIDES
OXYGEN COMPOUNDS
TESTING
TRANSITION ELEMENTS
YIELDS
010408* - Coal
Lignite
& Peat- C1 Processes- (1987-)