Differentiated use of refractories in blast-furnace hot blast stoves
Journal Article
·
· Refractories (Engl. Transl.); (United States)
OSTI ID:5281349
It is well known that the efficiency and coke utilization of a blast furnace can be increased if the operating temperature can be effectively raised within the furnace. To this end, the authors of this paper test a variety of heat-resistant refractories under increased thermal loads and comparatively assess their deformation and fracture behavior under these loads. Structural, mechanical and corrosive aspects are discussed.
- OSTI ID:
- 5281349
- Journal Information:
- Refractories (Engl. Transl.); (United States), Vol. 27:7-8; Other Information: Translated from Ogneupory; 27: No. 7, 44-50(Jul 1986)
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effect of chemical attack and operational parameters on the wear of blast furnace refractories
Hot repair of ceramic burner on hot blast stoves at USS/Kobe`s {number_sign}3 blast furnace
Blast-furnace operation on cokes made under differing carbonizing temperature conditions. [950 to 1050/sup 0/C coke finishing temperature]
Technical Report
·
Thu Jan 01 00:00:00 EST 1976
·
OSTI ID:5281349
Hot repair of ceramic burner on hot blast stoves at USS/Kobe`s {number_sign}3 blast furnace
Conference
·
Wed Dec 31 00:00:00 EST 1997
·
OSTI ID:5281349
+1 more
Blast-furnace operation on cokes made under differing carbonizing temperature conditions. [950 to 1050/sup 0/C coke finishing temperature]
Journal Article
·
Sat Jan 01 00:00:00 EST 1977
· Coke Chem., USSR (Engl. Transl.); (United States)
·
OSTI ID:5281349
+7 more
Related Subjects
32 ENERGY CONSERVATION, CONSUMPTION, AND UTILIZATION
36 MATERIALS SCIENCE
BLAST FURNACES
ENERGY EFFICIENCY
THERMAL INSULATION
REFRACTORIES
MATERIALS TESTING
TEMPERATURE EFFECTS
THERMAL CYCLING
THERMAL DEGRADATION
ALUMINIUM OXIDES
ALUMINIUM SILICATES
COKE
COMPARATIVE EVALUATIONS
CORROSION
CORUNDUM
CRACK PROPAGATION
DEFORMATION
FUEL ECONOMY
HEAT RESISTANT MATERIALS
LINERS
MAGNESIUM CARBONATES
MULLITE
SERVICE LIFE
SILICA
TEMPERATURE CONTROL
ALKALINE EARTH METAL COMPOUNDS
ALUMINIUM COMPOUNDS
CARBON COMPOUNDS
CARBONATES
CHALCOGENIDES
CHEMICAL REACTIONS
CONTROL
EFFICIENCY
FURNACES
INORGANIC ION EXCHANGERS
ION EXCHANGE MATERIALS
MAGNESIUM COMPOUNDS
MATERIALS
MINERALS
OXIDE MINERALS
OXIDES
OXYGEN COMPOUNDS
SILICATES
SILICON COMPOUNDS
SILICON OXIDES
TESTING
320302* - Energy Conservation
Consumption
& Utilization- Industrial & Agricultural Processes- Materials
360205 - Ceramics
Cermets
& Refractories- Corrosion & Erosion
360203 - Ceramics
Cermets
& Refractories- Mechanical Properties
360202 - Ceramics
Cermets
& Refractories- Structure & Phase Studies
36 MATERIALS SCIENCE
BLAST FURNACES
ENERGY EFFICIENCY
THERMAL INSULATION
REFRACTORIES
MATERIALS TESTING
TEMPERATURE EFFECTS
THERMAL CYCLING
THERMAL DEGRADATION
ALUMINIUM OXIDES
ALUMINIUM SILICATES
COKE
COMPARATIVE EVALUATIONS
CORROSION
CORUNDUM
CRACK PROPAGATION
DEFORMATION
FUEL ECONOMY
HEAT RESISTANT MATERIALS
LINERS
MAGNESIUM CARBONATES
MULLITE
SERVICE LIFE
SILICA
TEMPERATURE CONTROL
ALKALINE EARTH METAL COMPOUNDS
ALUMINIUM COMPOUNDS
CARBON COMPOUNDS
CARBONATES
CHALCOGENIDES
CHEMICAL REACTIONS
CONTROL
EFFICIENCY
FURNACES
INORGANIC ION EXCHANGERS
ION EXCHANGE MATERIALS
MAGNESIUM COMPOUNDS
MATERIALS
MINERALS
OXIDE MINERALS
OXIDES
OXYGEN COMPOUNDS
SILICATES
SILICON COMPOUNDS
SILICON OXIDES
TESTING
320302* - Energy Conservation
Consumption
& Utilization- Industrial & Agricultural Processes- Materials
360205 - Ceramics
Cermets
& Refractories- Corrosion & Erosion
360203 - Ceramics
Cermets
& Refractories- Mechanical Properties
360202 - Ceramics
Cermets
& Refractories- Structure & Phase Studies