Preparation of ultrathin supported solid electrolyte membranes for oxygen separation
- Max-Planck-Institut fuer Kohlenforschung, Ruhr (Germany)
Solid electrolyte layers active in oxygen ionic conductivity were prepared on mesoporous support membranes using physical vapor deposition methods. Gas separation studies were performed with for zirconia, bismuth-molybdate, and lead magnesium oxide membranes. Enhancement of oxygen permeability at higher temperatures due to ionic conductivity was possibly observed for the latter two film materials.
- OSTI ID:
- 518364
- Journal Information:
- Chemistry of Materials, Vol. 8, Issue 12; Other Information: PBD: Dec 1996
- Country of Publication:
- United States
- Language:
- English
Similar Records
SUPPORTED DENSE CERAMIC MEMBRANES FOR OXYGEN SEPARATION
Oxygen permeation through electrochemical vapor deposited solid oxide membranes
SUPPORTED DENSE CERAMIC MEMBRANES FOR OXYGEN SEPARATION
Technical Report
·
Fri Jun 30 00:00:00 EDT 2000
·
OSTI ID:518364
Oxygen permeation through electrochemical vapor deposited solid oxide membranes
Conference
·
Sat Dec 31 00:00:00 EST 1994
·
OSTI ID:518364
SUPPORTED DENSE CERAMIC MEMBRANES FOR OXYGEN SEPARATION
Technical Report
·
Sat Mar 01 00:00:00 EST 2003
·
OSTI ID:518364