High-temperature dc superconducting quantum interference device with deep-submicron YBa sub 2 Cu sub 3 O sub 7 weak links
Journal Article
·
· Applied Physics Letters; (United States)
- Department of Physics, Boston University, Boston, Massachusetts (USA)
- AT T Bell Laboratories, Holmdel, New Jersey (USA)
We have fabricated a YBa{sub 2}Cu{sub 3}O{sub 7} (YBCO) thin-film dc superconducting quantum interference device (SQUID) with lithographically defined deep-submicron weak links. At 77 K the voltage response to dc flux is sinusoidal and nonhysteretic, with maximum peak-to-peak amplitude of 5 {mu}V. The maximum response is 8 {mu}V at 70 K, where 2{ital LI}{sub 0}/{Phi}{sub 0}{approx}1. At lower temperatures, the maximum response oscillates in the range 4--6 {mu}V. Random telegraph noise was observed near 30--40 K. Well-behaved Shapiro steps were observable at all measured temperatures below {ital T}{sub {ital c}}.
- OSTI ID:
- 5150197
- Journal Information:
- Applied Physics Letters; (United States), Vol. 59:20; ISSN 0003-6951
- Country of Publication:
- United States
- Language:
- English
Similar Records
Low 1/ f noise single-layer YBa sub 2 Cu sub 3 O sub x dc SQUID at 77 K
dc SQUID made of Ag-doped YBa sub 2 Cu sub 3 O sub 7 a - b plane-edge junctions
An ion-beam-assisted process for high-T{sub c} Josephson junctions
Journal Article
·
Mon Jun 15 00:00:00 EDT 1992
· Applied Physics Letters; (United States)
·
OSTI ID:5150197
+6 more
dc SQUID made of Ag-doped YBa sub 2 Cu sub 3 O sub 7 a - b plane-edge junctions
Journal Article
·
Mon Dec 30 00:00:00 EST 1991
· Applied Physics Letters; (United States)
·
OSTI ID:5150197
+1 more
An ion-beam-assisted process for high-T{sub c} Josephson junctions
Journal Article
·
Wed Oct 01 00:00:00 EDT 1997
· Applied Physics Letters
·
OSTI ID:5150197
+4 more
Related Subjects
75 CONDENSED MATTER PHYSICS
SUPERCONDUCTIVITY AND SUPERFLUIDITY
BARIUM OXIDES
SQUID DEVICES
CUPRATES
FABRICATION
YTTRIUM OXIDES
HIGH-TC SUPERCONDUCTORS
LOW TEMPERATURE
PERFORMANCE
QUATERNARY COMPOUNDS
ALKALINE EARTH METAL COMPOUNDS
AMINES
AMMONIUM COMPOUNDS
BARIUM COMPOUNDS
CHALCOGENIDES
COPPER COMPOUNDS
ELECTRONIC EQUIPMENT
EQUIPMENT
FLUXMETERS
MEASURING INSTRUMENTS
MICROWAVE EQUIPMENT
ORGANIC COMPOUNDS
OXIDES
OXYGEN COMPOUNDS
SUPERCONDUCTING DEVICES
SUPERCONDUCTORS
TRANSITION ELEMENT COMPOUNDS
YTTRIUM COMPOUNDS
426001* - Engineering- Superconducting Devices & Circuits- (1990-)
SUPERCONDUCTIVITY AND SUPERFLUIDITY
BARIUM OXIDES
SQUID DEVICES
CUPRATES
FABRICATION
YTTRIUM OXIDES
HIGH-TC SUPERCONDUCTORS
LOW TEMPERATURE
PERFORMANCE
QUATERNARY COMPOUNDS
ALKALINE EARTH METAL COMPOUNDS
AMINES
AMMONIUM COMPOUNDS
BARIUM COMPOUNDS
CHALCOGENIDES
COPPER COMPOUNDS
ELECTRONIC EQUIPMENT
EQUIPMENT
FLUXMETERS
MEASURING INSTRUMENTS
MICROWAVE EQUIPMENT
ORGANIC COMPOUNDS
OXIDES
OXYGEN COMPOUNDS
SUPERCONDUCTING DEVICES
SUPERCONDUCTORS
TRANSITION ELEMENT COMPOUNDS
YTTRIUM COMPOUNDS
426001* - Engineering- Superconducting Devices & Circuits- (1990-)