Banded structures in directionally solidified Ti-52Al alloys
Journal Article
·
· Scripta Metallurgica et Materialia; (United States)
- Univ. of Birmingham (United Kingdom)
- Univ. of Birmingham (United Kingdom). School of Metallurgy and Materials
The authors report their results on the structure and chemistry of ingots and directionally solidified Ti-48Al and Ti-52Al alloys. Through the banding behavior, quantitative analysis of parts of the high temperature phase field in near-equiatomic Ti-Al alloys is obtained. A possible explanation for certain puzzling and unexplained observations by Oliver is presented. Optical microscopy, electron probe microanalysis (EPMA), scanning electron microscopy (SEM) and transmission electron microscopy (TEM) were used in this investigation.
- OSTI ID:
- 5055371
- Journal Information:
- Scripta Metallurgica et Materialia; (United States), Vol. 30:6; ISSN 0956-716X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Microstructural characterization of Ti-44Al-11Nb in the chill-cast and directionally solidified configurations
Establishing a Scientific Basis for Optimizing Compositions, Process Paths and Fabrication Methods for Nanostructured Ferritic Alloys for Use in Advanced Fission Energy Systems
Orientation imaging of a Nb-Ti-Si directionally solidified in-situ composite
Thesis/Dissertation
·
Tue Dec 01 00:00:00 EST 1998
·
OSTI ID:5055371
Establishing a Scientific Basis for Optimizing Compositions, Process Paths and Fabrication Methods for Nanostructured Ferritic Alloys for Use in Advanced Fission Energy Systems
Technical Report
·
Tue Feb 21 00:00:00 EST 2012
·
OSTI ID:5055371
+1 more
Orientation imaging of a Nb-Ti-Si directionally solidified in-situ composite
Conference
·
Tue Dec 31 00:00:00 EST 1996
·
OSTI ID:5055371