Hydrogen embrittlement of PH 13-8 Mo stainless steel-the effect of surface condition
Journal Article
·
· Corrosion (Houston); (United States)
The susceptibility of precipitation hardening 13-8 Mo stainless steel to hydrogen embrittlement (HE) was measured by both post hydrogen charging tensile tests and by time to failure tests while being subjected to hydrogen charging and a static stress below the yield stress. In the former, it was found that the ductility was decreased substantially after only 30 min charging time. The strength was markedly reduced after 2 h charging time. In the delayed failure tests, it was found that a localized cold worked surface condition promoted crack formation.
- Research Organization:
- California Polytechnic State University, San Luis Obispo, California
- OSTI ID:
- 5033721
- Journal Information:
- Corrosion (Houston); (United States), Vol. 40:4
- Country of Publication:
- United States
- Language:
- English
Similar Records
Hydrogen embrittlement behavior of palladium modified PH 13-8 Mo stainless steel as a function of age hardening
HYDROGEN-EMBRITTLEMENT SUSCEPTIBILITY OF SOME STEELS AND NONFERROUS ALLOYS
TRITIUM AGING EFFECTS ON THE FRACTURE TOUGHNESS PROPERTIES OF STAINLESS STEEL BASE METAL AND WELDS
Journal Article
·
Fri Jul 15 00:00:00 EDT 1994
· Scripta Metallurgica et Materialia; (United States)
·
OSTI ID:5033721
HYDROGEN-EMBRITTLEMENT SUSCEPTIBILITY OF SOME STEELS AND NONFERROUS ALLOYS
Technical Report
·
Mon Oct 19 00:00:00 EDT 1959
·
OSTI ID:5033721
TRITIUM AGING EFFECTS ON THE FRACTURE TOUGHNESS PROPERTIES OF STAINLESS STEEL BASE METAL AND WELDS
Conference
·
Thu Jul 30 00:00:00 EDT 2009
·
OSTI ID:5033721
Related Subjects
36 MATERIALS SCIENCE
MOLYBDENUM ALLOYS
FRACTURE PROPERTIES
HYDROGEN EMBRITTLEMENT
PRECIPITATION HARDENING
SURFACE PROPERTIES
STAINLESS STEELS
CRACK PROPAGATION
DESTRUCTIVE TESTING
FRACTURE MECHANICS
PHYSICAL METALLURGY
STATIC LOADS
STRESS ANALYSIS
STRESSES
TENSILE PROPERTIES
ALLOYS
CHROMIUM ALLOYS
CORROSION RESISTANT ALLOYS
EMBRITTLEMENT
HARDENING
IRON ALLOYS
IRON BASE ALLOYS
MATERIALS TESTING
MECHANICAL PROPERTIES
MECHANICS
METALLURGY
STEELS
TESTING
360103* - Metals & Alloys- Mechanical Properties
MOLYBDENUM ALLOYS
FRACTURE PROPERTIES
HYDROGEN EMBRITTLEMENT
PRECIPITATION HARDENING
SURFACE PROPERTIES
STAINLESS STEELS
CRACK PROPAGATION
DESTRUCTIVE TESTING
FRACTURE MECHANICS
PHYSICAL METALLURGY
STATIC LOADS
STRESS ANALYSIS
STRESSES
TENSILE PROPERTIES
ALLOYS
CHROMIUM ALLOYS
CORROSION RESISTANT ALLOYS
EMBRITTLEMENT
HARDENING
IRON ALLOYS
IRON BASE ALLOYS
MATERIALS TESTING
MECHANICAL PROPERTIES
MECHANICS
METALLURGY
STEELS
TESTING
360103* - Metals & Alloys- Mechanical Properties