Application-oriented characterization of Sm{sub 2}(Co,Fe,Cu,Zr){sub 17} permanent magnets
- Univ. of Dayton Magnetics Lab., OH (United States)
- Aerospace Power Div., Wright-Patterson AFB, OH (United States)
Application-oriented characterizations were carried out for Sm{sub 2}(Co,Fe,Cu,Zr){sub 17} permanent magnets in which both high temperature effects and aging effect are taken into account. Experimental results indicate that application-oriented characterization may provide data more application-oriented than traditional high temperature aging test data. The irreversible loss of the maximum energy product of Sm{sub 2}(Co,Fe,Cu,Zr){sub 17} caused from thermal demagnetization increases rapidly with temperature. It should be possible to reduce this loss by optimizing magnet compositions and heat treatments, which would significantly improve the high temperature performance of Sm{sub 2}(Co,Fe,Cu,Zr){sub 17} magnets.
- OSTI ID:
- 403176
- Report Number(s):
- CONF-960425-; ISSN 0018-9464; TRN: IM9651%%211
- Journal Information:
- IEEE Transactions on Magnetics, Vol. 32, Issue 5Pt2; Conference: 1996 IEEE international magnetics conference, Seattle, WA (United States), 9-12 Apr 1996; Other Information: PBD: Sep 1996
- Country of Publication:
- United States
- Language:
- English
Similar Records
The effect of Fe content on the temperature dependent magnetic properties of Sm(Co,Fe,Cu,Zr){sub z} and SmCo{sub 5} sintered magnets at 450 C
Enhancement of the magnetic properties of the Sm/sub 2/Cu/sub 1. 6/Zr/sub 0. 16/Fe/sub 3. 3/Co/sub 12/ compound