The inhomogeneity of a Langmuir-Blodgett film was evaluated from the halfwidth and the maximum intensity of the Bragg reflection peak measured in double-crystal X-ray diffraction studies. The mean square values of the internal stresses and the angle between mosaic blocks were determined, as well as the film roughness. The effect of internal elastic stress relaxation due to the change in the mosaic-block misorientation is established. 11 refs., 4 figs.
- OSTI ID:
- 379307
- Journal Information:
- Crystallography Reports, Vol. 39, Issue 6; Other Information: PBD: 1994; TN: Translated from Kristallografiya; 39: No. 6, 1115-1118(1994)
- Country of Publication:
- United States
- Language:
- English
Similar Records
Langmuir-Blodgett films of random copolymers of fluoroalkyl(meth)acrylate and methacrylic acid: Fabrication and X-ray diffraction study
Oriented polyvinylidene fluoride–trifluoroethylene (P(VDF–TrFE)) films by Langmuir–Blodgett deposition: A synchrotron X-ray diffraction study
Preparation and characterization of Langmuir and Langmuir Blodgett films
Book
·
Sat Dec 31 00:00:00 EST 1994
·
OSTI ID:379307
+1 more
Oriented polyvinylidene fluoride–trifluoroethylene (P(VDF–TrFE)) films by Langmuir–Blodgett deposition: A synchrotron X-ray diffraction study
Journal Article
·
Wed Oct 07 00:00:00 EDT 2015
· Physical Chemistry Chemical Physics. PCCP (Print)
·
OSTI ID:379307
+6 more
Preparation and characterization of Langmuir and Langmuir Blodgett films
Journal Article
·
· Appl. Phys. Commun.; (United States)
·
OSTI ID:379307