A study of highly oriented pyrolytic graphite as a model for the graphite anode in Li-ion batteries
- Tel Aviv Univ. (Israel)
The mechanisms of oxidation of the basal plane and of the cross-sectional face of highly oriented pyrolytic graphite (HOPG) and the formation of a solid electrolyte interphase (SEI) on HOPG samples that were cycled in ethylene carbonate:diethyl carbonate (EC:DEC 1:2) solutions containing 1 M LiAsF{sub 6} were studied. X-ray photoelectron spectroscopy, energy dispersive spectrometry, and scanning electron microscope techniques were used for the analysis of the surface layer formed on the basal plane and cross section of HOPG. The analysis indicates that the oxidation mechanisms of the basal plane and the cross section are entirely different. The SEI formed in the LiAsF{sub 6} solution is thinner on the basal plane than on the cross section and its composition is different. The SEI formed on the cross section is rich in inorganic compounds whereas the SEI formed on the basal plane is rich in organic compounds. Thus it can be concluded that on the basal plane, the greatest contribution to SEI formation is solvent reduction (EC and DEC), whereas on the cross-sectional face, it is electrolyte salt (LiAsF{sub 6}) reduction.
- OSTI ID:
- 345366
- Journal Information:
- Journal of the Electrochemical Society, Vol. 146, Issue 3; Other Information: PBD: Mar 1999
- Country of Publication:
- United States
- Language:
- English
Similar Records
Template electropolymerization of polypyrrole nanostructures on highly ordered pyrolytic graphite step and pit defects
A Comparison of Solid Electrolyte Interphase Formation and Evolution on Highly Oriented Pyrolytic and Disordered Graphite Negative Electrodes in Lithium–Ion Batteries