Formation of hot particles during the Chernobyl nuclear power plant accident
- Ukrainian Inst. of Agricultural Radiology, Chabany (Ukraine)
The oxidation of irradiated Chernobyl nuclear fuel at 670 to 1,170 K for 3 to 21 h resulted in its destruction into fine particles, the dispersal composition of which is well described by lognormal distribution regularity. The median radius of the formed particles does not depend on the annealing temperature and decreases with the increase of the annealing period from 10 to 3 {micro}m. Proceeding from the dispersal composition and matrix composition of the Chernobyl hot fuel particles, it can be concluded that the oxidation of nuclear fuel was one of the basic mechanisms of hot fuel particle formation during the accident at the Chernobyl nuclear power plant. With oxidation in air and the dispersal of irradiated oxide nuclear fuel at as low as 670 K, ruthenium, located on the granular borders, is released. Ruthenium is oxidized to volatile RuO{sub 4}, sublimated, and condensed on materials of iron. Nickel and stainless steel can be efficiently used at high temperatures (tested to 1,200 K) for radioruthenium adsorption in accidents and for some technological operations. As the temperature of hot fuel particles annealed in inert media increases from 1,270 to 2,270 K, the relative release of radionuclides increases in the following sequence: cesium isotopes; europium isotopes; cerium isotopes; americium isotopes; and ruthenium, plutonium, and curium isotopes.
- OSTI ID:
- 248115
- Journal Information:
- Nuclear Technology, Vol. 114, Issue 2; Other Information: PBD: May 1996
- Country of Publication:
- United States
- Language:
- English
Similar Records
Reconstruction of transuranium radionuclide radiation dose to the population in regions far from the Chernobyl accident
General classification of ``hot`` particles from the nearest Chernobyl contaminated areas