Dielectric relaxation and magnetodielectric response in DyMn{sub 0.5}Cr{sub 0.5}O{sub 3}
- Key Laboratory of Materials Physics, Institute of Solid State Physics, Chinese Academy of Sciences, Hefei 230031 (China)
We investigate the structural, magnetic, and magnetodielectric properties of DyMn{sub 0.5}Cr{sub 0.5}O{sub 3}. The sample can be indexed with an orthorhombic phase with B site disordered space group Pbnm. The valence state of both Mn and Cr ions are suggested to be +3 based on the results of x-ray photoelectron spectroscopy. Two thermally excited dielectric relaxation at temperatures T{sub N2} < T< 300 K and large magnetodielectric effect (MDC = 20%–30%) due to the disordered arrangement of Mn{sup 3+}/Cr{sup 3+} ions associated with electron hopping between them are observed. The absence of any noticeable magnetoresistance effect (MR < 0.5%) demonstrates that the observed magnetodielectric effect is an intrinsic behavior. These results suggest that DyMn{sub 0.5}Cr{sub 0.5}O{sub 3} is a magnetodielectric compound, whose dielectric properties are dependence of the applied magnetic field, which exhibits such effects near room temperature and holds great promise for future device applications.
- OSTI ID:
- 22492720
- Journal Information:
- Journal of Applied Physics, Vol. 118, Issue 12; Other Information: (c) 2015 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0021-8979
- Country of Publication:
- United States
- Language:
- English
Similar Records
Low temperature magneto-dielectric measurements on BiFeO{sub 3} lightly substituted by cobalt
Structural, magnetic, and dielectric studies of the Aurivillius compounds SrBi{sub 5}Ti{sub 4}MnO{sub 18} and SrBi{sub 5}Ti{sub 4}Mn{sub 0.5}Co{sub 0.5}O{sub 18}
Related Subjects
SUPERCONDUCTIVITY AND SUPERFLUIDITY
71 CLASSICAL AND QUANTUM MECHANICS
GENERAL PHYSICS
CHROMIUM IONS
DIELECTRIC MATERIALS
DIELECTRIC PROPERTIES
MAGNETIC FIELDS
MAGNETORESISTANCE
MANGANESE IONS
ORTHORHOMBIC LATTICES
RELAXATION
SPACE GROUPS
TEMPERATURE RANGE 0273-0400 K
X-RAY PHOTOELECTRON SPECTROSCOPY