Pressure-induced kinetics of the α to ω transition in zirconium
- HPCAT, Geophysical Laboratory, Carnegie Institution of Washington, Washington, DC 20015 (United States)
Diamond anvil cells (DAC) coupled with x-ray diffraction (XRD) measurements are one of the primary techniques for investigating structural stability of materials at high pressure-temperature (P-T) conditions. DAC-XRD has been predominantly used to resolve structural information at set P-T conditions and, consequently, provides P-T phase diagram information on a broad range of materials. With advances in large scale synchrotron x-ray facilities and corresponding x-ray diagnostic capabilities, it is now becoming possible to perform sub-second time resolved measurements on micron sized DAC samples. As a result, there is an opportunity to gain valuable information about the kinetics of structural phase transformations and extend our understanding of material behavior at high P-T conditions. Using DAC-XRD time resolved measurements, we have investigated the kinetics of the α to ω transformation in zirconium. We observe a clear time and pressure dependence in the martensitic α-ω transition as a function of pressure-jump, i.e., drive pressure. The resulting data are fit using available kinetics models, which can provide further insight into transformation mechanism that influence transformation kinetics. Our results help shed light on the discrepancies observed in previous measurements of the α-ω transition pressure in zirconium.
- OSTI ID:
- 22490788
- Journal Information:
- Journal of Applied Physics, Vol. 118, Issue 2; Other Information: (c) 2015 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0021-8979
- Country of Publication:
- United States
- Language:
- English
A Model for Phase Transitions Under Dynamic Compression
|
journal | October 2016 |
Room-temperature compression and equation of state of body-centered cubic zirconium
|
journal | December 2019 |
Similar Records
Time-resolved x-ray diffraction and electrical resistance measurements of structural phase transitions in zirconium
Real time study of grain enlargement in zirconium under room-temperature compression across the α to ω phase transition