Synthesis, characterization and hydrogen storage studies on porous carbon
Journal Article
·
· AIP Conference Proceedings
- Chemistry Division, Bhabha Atomic Research Centre, Trombay, Mumbai-400085 (India)
- High Pressure& Synchrotron Radiation Physics Division, Bhabha Atomic Research Centre, Mumbai-400085 (India)
Porous carbon sample has been prepared, using zeolite-Y as template followed by annealing at 800°C, with view to estimate the extent of hydrogen storage by the sample. Based on XRD, {sup 13}C MAS NMR and Raman spectroscopic studies it is confirmed that the porous Carbon sample contains only sp{sup 2} hybridized carbon. The hydrogen sorption isotherms have been recorded for the sample at 273, 223K and 123K and the maximum hydrogen absorption capacity is found to be 1.47wt% at 123K. The interaction energy of hydrogen with the carbon framework was determined to be ∼ 10 kJ mol{sup −1}at lower hydrogen uptake and gradually decreases with increase in hydrogen loading.
- OSTI ID:
- 22490621
- Journal Information:
- AIP Conference Proceedings, Vol. 1665, Issue 1; Conference: 59. DAE solid state physics symposium 2014, Tamilnadu (India), 16-20 Dec 2014; Other Information: (c) 2015 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Highly porous organic polymers bearing tertiary amine group and their exceptionally high CO{sub 2} uptake capacities
Preparation and characterization of ordered porous carbons for increasing hydrogen storage behaviors
A porous open-framework titanium oxophenylphosphate
Journal Article
·
Sun Feb 15 00:00:00 EST 2015
· Journal of Solid State Chemistry
·
OSTI ID:22490621
Preparation and characterization of ordered porous carbons for increasing hydrogen storage behaviors
Journal Article
·
Sat Oct 15 00:00:00 EDT 2011
· Journal of Solid State Chemistry
·
OSTI ID:22490621
A porous open-framework titanium oxophenylphosphate
Journal Article
·
Fri Aug 15 00:00:00 EDT 2008
· Journal of Solid State Chemistry
·
OSTI ID:22490621
+1 more