Influence of calcium on structural and morphological properties of BiMnO{sub 3} thin films
Journal Article
·
· AIP Conference Proceedings
- Materials Physics Division, School of Advanced Sciences, VIT University, Vellore-632014 (India)
Bi{sub 1-x}Ca{sub x}MnO{sub 3} (x = 0, 0.1, 0.2, 0.4) thin films were deposited on n–type silicon (100) substrate by RF magnetron sputtering. The X-ray diffraction pattern showed that the films were in monoclinic structure with C2 space group. The crystallite size and strain in the prepared films were measured by W-H plot. The surface morphology of the films was examined by atomic force microscope. The thickness of films was measured by thickness monitor in the sputtering system. From the analysis, it has been concluded that the optimum level for calcium doping is 20 at.% in the Bi site of BiMnO{sub 3} thin film, which will lead a way for further research in the Ca doped BiMnO{sub 3} system.
- OSTI ID:
- 22490429
- Journal Information:
- AIP Conference Proceedings, Vol. 1665, Issue 1; Conference: 59. DAE solid state physics symposium 2014, Tamilnadu (India), 16-20 Dec 2014; Other Information: (c) 2015 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Structural and morphological studies on Bi{sub 1-x}Ca{sub x}MnO{sub 3} thin films grown by RF magnetron sputtering
Room temperature ferromagnetic and ferroelectric properties of Bi{sub 1−x}Ca{sub x}MnO{sub 3} thin films
Ferromagnetism and ferroelectricity in epitaxial BiMnO{sub 3} ultra-thin films
Journal Article
·
Mon May 23 00:00:00 EDT 2016
· AIP Conference Proceedings
·
OSTI ID:22490429
Room temperature ferromagnetic and ferroelectric properties of Bi{sub 1−x}Ca{sub x}MnO{sub 3} thin films
Journal Article
·
Sat Nov 15 00:00:00 EST 2014
· AIP Advances
·
OSTI ID:22490429
Ferromagnetism and ferroelectricity in epitaxial BiMnO{sub 3} ultra-thin films
Journal Article
·
Mon Aug 05 00:00:00 EDT 2013
· Applied Physics Letters
·
OSTI ID:22490429
+4 more