(Pt{sub 1–x}Cu{sub x}){sub 3}Cu{sub 2}B and Pt{sub 9}Cu{sub 3}B{sub 5}, the first examples of copper platinum borides. Observation of superconductivity in a novel boron filled β-Mn-type compound
- Institute of Solid State Physics, TU Wien, A-1040 Wien (Austria)
- Institute of Chemical Technologies and Analytics, TU Wien, A-1040 Wien (Austria)
- Institute of Physical Chemistry, University of Vienna, A-1090 Wien (Austria)
New ternary copper platinum borides have been synthesized by arc melting of pure elements followed by annealing at 600 °C. The structures have been studied by X-ray single crystal and powder diffraction. (Pt{sub 1−x}Cu{sub x}){sub 3}Cu{sub 2}B (x=0.33) forms a B-filled β-Mn-type structure (space group P4{sub 1}32; a=0.6671(1) nm). Cu atoms are distributed preferentially on the 8c atom sites, whereas the 12d site is randomly occupied by Pt and Cu atoms (0.670(4) Pt±0.330(4) Cu). Boron is located in octahedral voids of the parent β-Mn-type structure. Pt{sub 9}Cu{sub 3}B{sub 5} (space group P-62m; a=0.9048(3) nm, c=0.2908(1) nm) adopts the Pt{sub 9}Zn{sub 3}B{sub 5–δ}-type structure. It has a columnar architecture along the short translation vector exhibiting three kinds of [Pt{sub 6}] trigonal prism columns (boron filled, boron semi-filled and empty) and Pt channels with a pentagonal cross section filled with Cu atoms. The striking structural feature is a [Pt{sub 6}] cluster in form of an empty trigonal prism at the origin of the unit cell, which is surrounded by coupled [BPt{sub 6}] and [Pt{sub 6}] trigonal prisms, rotated perpendicularly to the central one. There is no B–B contact as well as Cu–B contact in the structure. The relationships of Pt{sub 9}Cu{sub 3}B{sub 5} structure with the structure of Ti{sub 1+x}Os{sub 2−x}RuB{sub 2} as well as with the structure families of metal sulfides and aluminides have been elucidated. (Pt{sub 1–x}Cu{sub x}){sub 3}Cu{sub 2}B (x=0.3) (B-filled β-Mn-type structure) is a bulk superconductor with a transition temperature of about 2.06 K and an upper critical field μ{sub 0}H{sub C2}(0){sup WHH} of 1.2 T, whereas no superconducting transition has been observed up to 0.3 K in Pt{sub 9}Cu{sub 3}B{sub 5} (Pt{sub 9}Zn{sub 3}B{sub 5–δ}-type structure) from electrical resistivity measurements. - Highlights: • First two copper platinum borides, (Pt{sub 0.67}Cu{sub 0.33}){sub 3}Cu{sub 2}B and Pt{sub 9}Cu{sub 3}B{sub 5} were obtained. • (Pt{sub 0.67}Cu{sub 0.33}){sub 3}Cu{sub 2}B forms a B-filled β-Mn-type structure. • Pt{sub 9}Cu{sub 3}B{sub 5} adopts a Pt{sub 9}Zn{sub 3}B{sub 5–δ}-type structure. • Boron atoms exhibit octahedral and trigonal prismatic coordination. • (Pt{sub 1–x}Cu{sub x})3Cu{sub 2}B (x=0.3) is a bulk superconductor with T{sub c} 2.06 K.
- OSTI ID:
- 22486778
- Journal Information:
- Journal of Solid State Chemistry, Vol. 229; Other Information: Copyright (c) 2015 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0022-4596
- Country of Publication:
- United States
- Language:
- English
Similar Records
In{sub 3}Ir{sub 3}B, In{sub 3}Rh{sub 3}B and In{sub 5}Ir{sub 9}B{sub 4}, the first indium platinum metal borides
Commensurate and incommensurate phases in the system A{sub 4}A{prime}Ir{sub 2}O{sub 9} (A = Sr, Ba; A{prime} = Cu, Zn)
Related Subjects
SUPERCONDUCTIVITY AND SUPERFLUIDITY
37 INORGANIC
ORGANIC
PHYSICAL AND ANALYTICAL CHEMISTRY
ANNEALING
BORON
COPPER
COPPER BORIDES
CRITICAL FIELD
CUBIC LATTICES
MELTING
PLATINUM
PLATINUM COMPOUNDS
SULFIDES
SUPERCONDUCTIVITY
SUPERCONDUCTORS
TRANSITION TEMPERATURE
X-RAY DIFFRACTION