Structure and ionic conductivity of well-aligned polycrystalline sodium titanogallate grown by reactive diffusion

Journal Article · Tue Sep 15 00:00:00 EDT 2015 · Journal of Solid State Chemistry

DOI:https://doi.org/10.1016/J.JSSC.2015.06.005· OSTI ID:22486772

Hasegawa, Ryo; Okabe, Momoko; Asaka, Toru ^[1]; Ishizawa, Nobuo ^[2]; Fukuda, Koichiro ^[1]

---

1. Department o f Materials Science and Engineering, Nagoya Institute of Technology, Nagoya 466-8555 (Japan)
2. Advanced Ceramics Research Center, Nagoya Institute of Technology, Tajimi 507-0071 (Japan)

We prepared the b-axis-oriented polycrystalline Na{sub 0.85}Ti{sub 0.51}Ga{sub 4.37}O{sub 8} (NTGO) embedded in Ga{sub 2}O{sub 3}-doped Na{sub 2}Ti{sub 4}O{sub 9} matrix using the reactive diffusion technique. When the sandwich-type Ga{sub 2}TiO{sub 5}/NaGaO{sub 2}/Ga{sub 2}TiO{sub 5} diffusion couple was heated at 1323 K for 24 h, the NTGO polycrystal was readily formed in the presence of a liquid phase. The resulting polycrystalline material was characterized by X-ray diffractometry, electron microscopy and impedance spectroscopy. We mechanically processed the annealed diffusion couple and obtained the thin-plate electrolyte consisting mostly of the grain-aligned NTGO polycrystal. The ionic conductivity (σ) of the electrolyte along the common b-axis direction steadily increased from 1.3×10{sup −4} to 7.3×10{sup −3} S/cm as the temperature increased from 573 to 1073 K. There was a slope change at ca. 792 K for the Arrhenius plot of σ; the activation energies were 0.39 eV above this temperature and 0.57 eV below it. The NTGO showed the crystal structure (space group C2/m) with substantial positional disordering of one of the two Ga sites. The Na{sup +} ions occupied ca. 43% of the Wyckoff position 4i site, the deficiency of which would contribute to the relatively high ionic conductivity along the b-axis. The reactive diffusion could be widely applicable as the novel technique to the preparation of grain-aligned ceramics of multi-component systems. - Graphical abstract: We have prepared the b-axis-oriented Na{sub 0.85}Ti{sub 0.51}Ga{sub 4.37}O{sub 8} polycrystal embedded in Ga{sub 2}O{sub 3}-doped Na{sub 2}Ti{sub 4}O{sub 9} matrix by the heat treatment of sandwich-type diffusion couple of Ga{sub 2}TiO{sub 5}/NaGaO{sub 2}/Ga{sub 2}TiO{sub 5}. The resulting Na{sub 0.85}Ti{sub 0.51}Ga{sub 4.37}O{sub 8} electrolyte showed the ionic conductivity ranging from 1.3×10{sup −4} S/cm at 573 K to 7.3×10{sup −3} S/cm at 1073 K. - Highlights: • The b-axis-oriented polycrystalline Na{sub 0.85}Ti{sub 0.51}Ga{sub 4.37}O{sub 8} is successfully prepared. • Crystal structure of Na{sub 0.85}Ti{sub 0.51}Ga{sub 4.37}O{sub 8} is determined by single-crystal XRD. • The polycrystal shows relatively high Na{sup +} ion conductivity along the common b-axis. • Reactive diffusion is successfully used for the preparation of grain-aligned ceramics.

• OSTI ID: 22486772
• Journal Information: Journal of Solid State Chemistry, Vol. 229; Other Information: Copyright (c) 2015 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0022-4596
• Country of Publication: United States
• Language: English

Related Subjects

37 INORGANIC
ORGANIC
PHYSICAL AND ANALYTICAL CHEMISTRY
ACTIVATION ENERGY
ANNEALING
CERAMICS
DIFFUSION
DOPED MATERIALS
ELECTRIC CONDUCTORS
ELECTRON MICROSCOPY
GALLIUM OXIDES
IMPEDANCE
MATRIX MATERIALS
MONOCLINIC LATTICES
MONOCRYSTALS
PLATES
POLYCRYSTALS
SODIUM COMPOUNDS
SODIUM IONS
TITANATES
X-RAY DIFFRACTION