Effects of BiAlO{sub 3}-doping on dielectric and ferroelectric properties of 0.93Na{sub 0.5}Bi{sub 0.5}TiO{sub 3}–0.07BaTiO{sub 3} lead-free ceramics

Journal Article · Wed Jul 15 00:00:00 EDT 2015 · Materials Research Bulletin

DOI:https://doi.org/10.1016/J.MATERRESBULL.2015.03.012· OSTI ID:22475816

Wang, Jian; Chen, Xiao-ming; Zhao, Xu-mei; Liang, Xiao-xia; Zhou, Jian-ping; Liu, Peng

Highlights: • BiAlO{sub 3}-doped BNT-based ceramics were synthesized via a conventional solid state reaction method. • T% values are 56%, 32%, 37%, and 37% for the ceramics with x = 0, 0.01, 0.02 and 0.06, respectively. • The mean grain sizes of the ceramics with x = 0, 0.01, 0.02 and 0.06 are about 1.1, 0.9, 0.8 and 0.7 μm, respectively. • Dielectric anomalies in the ϵ{sub r}–T curves are close related to the BiAlO{sub 3} amounts. • The ceramic with x = 0.01 shows the P{sub m} of 32.5 μC/cm{sup 2}, P{sub r} of 24.1 μC/cm{sup 2}, E{sub c} of 20.0 kV/cm and d{sub 33} of 166 pC/N. - Abstract: (1 − x)(0.93Na{sub 0.5}Bi{sub 0.5}TiO{sub 3}–0.07BaTiO{sub 3})–xBiAlO{sub 3} (BNBT-xBA, x = 0, 0.01, 0.02, 0.06) lead-free ceramics were synthesized via a conventional solid state reaction method. Crystallite structure, microstructure, dielectric and ferroelectric properties of the BNBT–xBA ceramics were studied in detail. X-ray diffraction results show that all ceramics exhibit typical diffraction peaks of ABO{sub 3} perovskite structure. Scanning electron microscope images show that all samples have fine microstructures. Both Curie temperature and maximum dielectric constant vary with the change in the BiAlO{sub 3} amounts. The values of hysteresis loop squareness were calculated to be 1.26, 0.81, 0.51 and 0.36 for the ceramics with x = 0, 0.01, 0.02 and 0.06, respectively, indicating a decreased switching behavior of polarization. The changes in dielectric and ferroelectric properties of the ceramics are also discussed.

• OSTI ID: 22475816
• Journal Information: Materials Research Bulletin, Vol. 67; Other Information: Copyright (c) 2015 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0025-5408
• Country of Publication: United States
• Language: English

Related Subjects

36 MATERIALS SCIENCE
ALUMINATES
BARIUM COMPOUNDS
BISMUTH COMPOUNDS
CERAMICS
COMPOSITE MATERIALS
CURIE POINT
DOPED MATERIALS
FERROELECTRIC MATERIALS
GRAIN SIZE
HYSTERESIS
PERMITTIVITY
PEROVSKITE
POLARIZATION
SCANNING ELECTRON MICROSCOPY
SODIUM COMPOUNDS
SOLIDS
TITANATES
X-RAY DIFFRACTION