Growth and characterization of acentric BaHf(BO{sub 3}){sub 2} and BaZr(BO{sub 3}){sub 2}
- Institute of Low Temperature and Structure Research, Polish Academy of Sciences, P.O. Box 1410, 50-950 Wrocław 2 (Poland)
- Institute of Applied Physics, Military University of Technology, 2 Kaliskiego Str., 00-908 Warszawa (Poland)
Growth, single crystal X-ray diffraction, polarized Raman and infrared (IR) studies of BaHf(BO{sub 3}){sub 2} are presented. Raman and IR spectra of polycrystalline BaZr(BO{sub 3}){sub 2} are also reported to facilitate assignment of modes. BaHf(BO{sub 3}){sub 2} borate crystallizes in trigonal system, space group R3c, with lattice parameters: a=5.1540(4) Å, c=33.901(3) Å. It accommodates dolomite-like structure doubled in the c direction, which is built of alternating layers of HfO{sub 6} octahedra and BaO{sub 6} distorted trigonal prisms that are connected through borate groups. The obtained structural as well as spectroscopic data show that BaHf(BO{sub 3}){sub 2} is isostructural with BaZr(BO{sub 3}){sub 2} and the deviations from centrosymmetry is small. - Graphical abstract: Arrangement of BO{sub 3} groups in BaHf(BO{sub 3}){sub 2} along the c direction in one unit cell. Dark and light blue denote different borate groups. - Highlights: • BaHf(BO{sub 3}){sub 2} single crystals were grown. • X-ray diffraction showed that this borate crystallizes in the acentric R3c structure. • Raman and IR spectra were measured for BaHf(BO{sub 3}){sub 2} and BaZr(BO{sub 3}){sub 2}, respectively. • Assignment of modes is proposed.
- OSTI ID:
- 22475612
- Journal Information:
- Journal of Solid State Chemistry, Vol. 225; Other Information: Copyright (c) 2015 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0022-4596
- Country of Publication:
- United States
- Language:
- English
Similar Records
A New Family of Proton‐Conducting Electrolytes for Reversible Solid Oxide Cells: BaHf x Ce 0.8− x Y 0.1 Yb 0.1 O 3− δ
Transition-metal substitution in PbAlBO{sub 4}: Synthesis, structural and spectroscopic studies of manganese containing phases