Magnetic and electrical properties of Fe{sub 0.9}Ag{sub 0.1}In{sub 2.3}S{sub 4.4} single crystals
- National Academy of Sciences of Belarus, Scientific and Practical Materials Research Center (Belarus)
- Belarusian State University of Information and Radio Electronics (Belarus)
The magnetic and electrical properties of the Fe{sub 0.9}Ag{sub 0.1}In{sub 2.3}S{sub 4.4} single crystal are studied in the temperature range 4–300 K and in magnetic fields of 0–14 T. It is established that the sample under study is paramagnetic. In the ground state, short-range-order correlations typical of a spin glass with a freezing temperature of 10 K are detected. The magnetic ordering temperature is 15 K. The sample is a semiconductor with a resistivity of 3.5 kΩ cm at room temperature. For the Fe{sub 0.9}Ag{sub 0.1}In{sub 2.3}S{sub 4.4} single crystal, a mechanism for the formation of magnetic and electrical states is suggested.
- OSTI ID:
- 22469729
- Journal Information:
- Semiconductors, Vol. 49, Issue 10; Other Information: Copyright (c) 2015 Pleiades Publishing, Ltd.; Country of input: International Atomic Energy Agency (IAEA); ISSN 1063-7826
- Country of Publication:
- United States
- Language:
- English
Similar Records
The magnetic properties of Bi{sub 0.9}Ba{sub 0.1}Fe{sub 0.81}M{sub 0.09}Ti{sub 0.1}O{sub 3} solid solutions (M = Co, Mn, Sc, Al)
Magnetostriction and anisotropy of twin-free single-crystals Tb{sub 0.5}Dy{sub 0.5}(Fe{sub 0.9}Mn{sub 0.1}){sub 2}
Synthesis and catalytic application of nanofibrous La{sub 0.9}A{sub 0.1}MnO{sub 3} (A = Ca, Cu, Ag) with macroscopic shapes
Journal Article
·
Tue Nov 15 00:00:00 EST 2011
· Materials Research Bulletin
·
OSTI ID:22469729
+1 more
Magnetostriction and anisotropy of twin-free single-crystals Tb{sub 0.5}Dy{sub 0.5}(Fe{sub 0.9}Mn{sub 0.1}){sub 2}
Journal Article
·
Mon Apr 01 00:00:00 EST 1996
· Journal of Applied Physics
·
OSTI ID:22469729
+2 more
Synthesis and catalytic application of nanofibrous La{sub 0.9}A{sub 0.1}MnO{sub 3} (A = Ca, Cu, Ag) with macroscopic shapes
Journal Article
·
Tue Oct 15 00:00:00 EDT 2013
· Materials Research Bulletin
·
OSTI ID:22469729
+1 more