Nucleation and growth of damage in polycrystalline aluminum under dynamic tensile loading
- School of Science, Wuhan University of Technology, Wuhan, 430070 (China)
Plate-impact experiments were conducted to study the features and mechanisms of void nucleation and growth in the polycrystalline of pure aluminum under dynamic loading. Soft-recovered samples have been analyzed by metallographic microscopy, electron back scattering diffraction (EBSD), and synchrotron radiation x-ray tomography technology. It was found that most of the void nucleation in grains neared the boundaries of “weak-orientation” grains and grew toward the grain boundaries with fractured small grains around the boundaries. This was mainly caused by the accumulation and interaction of slip systems in the “weak-orientation” grains. In addition, the micro voids were nearly octahedron because the octahedral slip systems were formed by 8 slip planes in the polycrystalline of pure aluminum. The EBSD results are consistent with the three-dimensional structure observed by synchrotron radiation x-ray.
- OSTI ID:
- 22454472
- Journal Information:
- AIP Advances, Vol. 5, Issue 3; Other Information: (c) 2015 Author(s); Country of input: International Atomic Energy Agency (IAEA); ISSN 2158-3226
- Country of Publication:
- United States
- Language:
- English
Similar Records
Correlations Between Spall Damage Mode Preference and Microstructure in Shocked Polycrystalline Copper: A 3-D X-Ray Tomography Study
Grain boundary inter-connections in polycrystalline aluminum with random orientation