Oxygen exchange reaction kinetics for cerium(IV) oxide at 1000 °C
Bulk oxygen exchange rate kinetics on CeO{sub 2} at 1000 °C were observed to have a first order dependence on the fraction of reaction remaining and to be independent of oxygen partial pressure, total pressure, particle size, and specific surface area. This suggests that the exchange reaction is dominated by an internal chemical reaction that is occurring throughout the bulk of the material, and not at the material surface. Oxygen exchange rates were limited by this internal chemical reaction for all CeO{sub 2} powders studied (15 nm to −325 mesh), and had a rate constant of 1.19×10{sup −2} s{sup −1} with a time to completion of 617 s. These results are similar to the exchange rates observed previously on PuO{sub 2}, suggesting that oxygen exchange on PuO{sub 2} may also be dominated by an internal chemical reaction under similar conditions. This work will help guide future experiments on {sup 238}PuO{sub 2} oxygen exchange reactions. - Graphical abstract: Oxygen exchange kinetics on CeO{sub 2} at 1000 °C are independent of a wide range of experimental conditions and exhibit first-order chemical reaction kinetics. - Highlights: • Stable oxygen exchange rates obtained on a variety of CeO{sub 2} powders at 1000 °C. • Exchange rates are independent of atmospheric composition and specific surface area. • Exchange rates are limited by an internal chemical reaction, not a surface reaction. • CeO{sub 2} exchange rates appear similar to the rates observed on PuO{sub 2} at 1000 °C.
- OSTI ID:
- 22443419
- Journal Information:
- Journal of Solid State Chemistry, Vol. 218; Other Information: Copyright (c) 2014 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0022-4596
- Country of Publication:
- United States
- Language:
- English
Similar Records
Kinetic and structural studies of oxygen availability of the mixed oxides Pr{sub 1{minus}{ital x}}M{sub {ital x}}O{sub {ital y}} (M=Ce, Zr)
Dissolution of cerium(IV)-lanthanide(III) oxides: Comparative effect of chemical composition, temperature, and acidity