Growing antiphase-domain-free GaAs thin films out of highly ordered planar nanowire arrays on exact (001) silicon
We report the use of highly ordered, dense, and regular arrays of in-plane GaAs nanowires as building blocks to produce antiphase-domain-free GaAs thin films on exact (001) silicon. High quality GaAs nanowires were grown on V-grooved Si (001) substrates using the selective aspect ratio trapping concept. The 4.1% lattice mismatch has been accommodated by the initial GaAs, a few nanometer-thick with high density stacking faults. The bulk of the GaAs wires exhibited smooth facets and a low defect density. An unusual defect trapping mechanism by a “tiara”-like structure formed by Si undercuts was discovered. As a result, we were able to grow large-area antiphase-domain-free GaAs thin films out of the nanowires without using SiO{sub 2} sidewalls for defect termination. Analysis from XRD ω-rocking curves yielded full-width-at-half-maximum values of 238 and 154 arc sec from 900 to 2000 nm GaAs thin films, respectively, indicating high crystalline quality. The growth scheme in this work offers a promising path towards integrated III-V electronic, photonic, or photovoltaic devices on large scale silicon platform.
- OSTI ID:
- 22412656
- Journal Information:
- Applied Physics Letters, Vol. 106, Issue 7; Other Information: (c) 2015 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0003-6951
- Country of Publication:
- United States
- Language:
- English
Similar Records
Epitaxial (GaAs)[sub 1[minus]][sub [ital x]](Si[sub 2])[sub [ital x]] metastable alloys on GaAs(001) and (GaAs)[sub 1[minus]][sub [ital x]](Si[sub 2])[sub [ital x]] /GaAs strained-layer superlattices: Crystal growth, spinodal decomposition, and antiphase domains
GaAs on Si epitaxy by aspect ratio trapping: Analysis and reduction of defects propagating along the trench direction