An InP/Si heterojunction photodiode fabricated by self-aligned corrugated epitaxial lateral overgrowth
- Laboratory of Semiconductor Materials, Department of Materials and Nano Physics, School of Information and Communication Technology, KTH-Royal Institute of Technology, Electrum 229, Kista S-164 40 (Sweden)
An n-InP/p-Si heterojunction photodiode fabricated by corrugated epitaxial lateral overgrowth (CELOG) method is presented. N-InP/p-Si heterojunction has been achieved from a suitable pattern containing circular shaped openings in a triangular lattice on the InP seed layer on p-Si substrate and subsequent CELOG of completely coalesced n-InP. To avoid current path through the seed layer in the final photodiode, semi-insulating InP:Fe was grown with adequate thickness prior to n-InP growth in a low pressure hydride vapor phase epitaxy reactor. The n-InP/p-Si heterointerface was analyzed by scanning electron microscopy and Raman spectroscopy. Room temperature cross-sectional photoluminescence (PL) mapping illustrates the defect reduction effect in InP grown on Si by CELOG method. The InP PL intensity measured above the InP/Si heterojunction is comparable to that of InP grown on a native planar substrate indicating low interface defect density of CELOG InP despite of 8% lattice mismatch with Si. The processed n-InP/p-Si heterojunction photodiodes show diode characteristics from the current-voltage (I-V) measurements with a dark current density of 0.324 mA/cm{sup 2} at a reverse voltage of −1 V. Under the illumination of AM1.5 conditions, the InP/Si heterojunction photodiode exhibited photovoltaic effect with an open circuit voltage of 180 mV, a short circuit current density of 1.89 mA/cm{sup 2}, an external quantum efficiency of 4.3%, and an internal quantum efficiency of 6.4%. This demonstration of epitaxially grown InP/Si heterojunction photodiode will open the door for low cost and high efficiency solar cells and photonic integration of III-Vs on silicon.
- OSTI ID:
- 22402508
- Journal Information:
- Applied Physics Letters, Vol. 106, Issue 21; Other Information: (c) 2015 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0003-6951
- Country of Publication:
- United States
- Language:
- English
Similar Records
Characterization of Epitaxial Film Silicon Solar Cells Grown on Seeded Display Glass: Preprint
Deep traps and photo-electric properties of p-Si/MgO/n-Zn{sub 1−x}Mg{sub x}O heterojunction
Related Subjects
SUPERCONDUCTIVITY AND SUPERFLUIDITY
CRYSTAL DEFECTS
CURRENT DENSITY
DOPED MATERIALS
HETEROJUNCTIONS
INDIUM PHOSPHIDES
IRON
LAYERS
PHOTODIODES
PHOTOLUMINESCENCE
PHOTOVOLTAIC EFFECT
QUANTUM EFFICIENCY
RAMAN SPECTROSCOPY
SCANNING ELECTRON MICROSCOPY
SILICON
SOLAR CELLS
SUBSTRATES
TEMPERATURE RANGE 0273-0400 K
VAPOR PHASE EPITAXY